DISTITRON 420 C
Delivery specification of the liquid resin Distitron 420C
Properties
Test method
Unit
Typical value
Viscosity RVF at 25°C, s 3 rpm 20
GM025
mPa.s
900 - 1300
Monomer content
RS06C
%
24 - 29
Curing at 25°C with
0,6% Co 6% + 1,5% MEKP
Gel time
RS08G
min.sec
6.00 - 10.00
Curing time
RS08G
min.sec
21.00 - 33.00
Maximum temperature
RS08G
°C
90 - 120
Properties of the liquid resin Distitron 420C
Properties
Test method
Unit
Typical value
Appearance - colour
RS13F
-----
Neutral
Acid number
RS02C
mg KOH/g
16 - 23
Stability at 20°C in the dark
RS07G
months
3
Properties of cured unreinforced resin Distitron 420C
Properties
Test method
Unit
Typical value
Tensile strength
ISO 527-1993
MPa
10
Tensile modulus
ISO 527-1993
MPa
90
Elongation at break
ISO 527-1993
%
60,0
Glass transition
ASTM E 1545-00
ºC
30
Full data sheet
Contact
Close
DISTITRON 429 ESX20Q
Delivery specification of the liquid resin Distitron 429ESX20Q
Properties
Test method
Unit
Typical value
Viscosity RVF at 25°C, s 2 rpm 2
GM025
mPa.s
1700 - 2300
Viscosity RVF at 25°C, s 2 rpm 20
GM025
mPa.s
530 - 720
Monomer content
RS06C
%
40 - 45
Curing at 25°C with
1% MEKP
Gel time
RS08G
min.sec
34.00 - 41.00
Curing time
RS08G
min.sec
58.00 - 78.00
Maximum temperature
RS08G
°C
100 - 125
Properties of the liquid resin Distitron 429ESX20Q
Properties
Test method
Unit
Typical value
Appearance - colour
RS13F
-----
Opalescent bluish
Acid number
RS02C
mg KOH/g
13 - 19
Stability at 20°C in the dark
RS07G
months
3
Properties of cured unreinforced resin 429ESX20Q
Properties
Test method
Unit
Typical value
Tensile strength
ISO 527-1993
MPa
45
Tensile modulus
ISO 527-1993
MPa
4100
Elongation at break
ISO 527-1993
%
1,4
Flexural strength
ISO 178-2001
MPa
85
Flexural modulus
ISO 178-2001
MPa
4200
Heat deflection temperature
ISO 75 - 2:2004 Method A
°C
66
Barcol hardness at 25°C
ASTM D 2583-01
Unit
45
Full data sheet
Contact
Close
DISTITRON 429 EXZ
Delivery specification of the liquid resin Distitron 429EXZ
Properties
Test method
Unit
Value
Viscosity RVF at 25°C, s 2 rpm 2
GM025
mPa.s
1100 - 1600
Viscosity RVF at 25°C, s 2 rpm 20
GM025
mPa.s
370 - 530
Monomer content
RS06C
%
40 - 45
Curing at 25°C with
0,2% Co6% + 1% MEKP MEKP
Gel time
RS08G
min.sec
32.00 - 43.00
Curing time
RS08G
min.sec
55.00 - 80.00
Maximum temperature
RS08G
°C
95 - 125
Properties of the liquid resin Distitron 429EXZ
Properties
Test method
Unit
Value
Appearance - colour
RS13F
-----
Opalescent yellow-brown
Stability at 20°C in the dark
RS07G
months
3
Properties of cured unreinforced resin Distitron 429EXZ
Properties
Test method
Unit
Typical value
Tensile strength
ISO 527-1993
MPa
45
Tensile modulus
ISO 527-1993
MPa
3900
Elongation at break
ISO 527-1993
%
1,6
Flexural strength
ISO 178-2001
MPa
85
Flexural modulus
ISO 178-2001
MPa
4100
Heat deflection temperature
ISO 75 - 2:2004 Method A
°C
64
Glass transition
ASTM E 1545-00
°C
73
Barcol hardness at 25°C
ASTM D 2583-01
Unit
44
Full data sheet
Contact
Close
DISTITRON 429 SV1.3
Delivery specification of the liquid resin Distitron 429SV1.3
Properties
Test method
Unit
Typical value
Viscosity RVF at 25°C, s 2 rpm 20
GM025
mPa.s
110 - 150
Monomer content
RS06C
%
41 - 45
Curing at 20°C with
1,5% MEKP (on 50g of resin)
Gel time
RS08G
min.sec
9.00 - 12.00
Curing time
RS08G
min.sec
20.00 - 31.00
Maximum temperature
RS08G
°C
115 - 145
Properties of the liquid resin Distitron 429SV1.3
Properties
Test method
Unit
Typical value
Appearance - colour
RS13F
-----
Rosa
Acid number
RS02C
mg KOH/g
13 - 20
Stability at 20°C in the dark
RS07G
months
6
Properties of cured unreinforced resin Distitron 429SV1.3
Properties
Test method
Unit
Typical value
Tensile strength
ISO 527-1993
MPa
70
Tensile modulus
ISO 527-1993
MPa
3900
Elongation at break
ISO 527-1993
%
2,3
Flexural strength
ISO 178-2001
MPa
130
Flexural modulus
ISO 178-2001
MPa
4200
Heat deflection temperature
ISO 75 - 2:2004 Method A
°C
68
Glass transition
ASTM E 1545-00
°C
78
Barcol hardness at 25°C
ASTM D 2583-01
Unit
47
Full data sheet
Contact
Close
DISTITRON 429 V1.3
Delivery specification of the liquid resin Distitron 429V1.3
Properties
Test method
Unit
Typical value
Viscosity RVF at 25°C, s 2 rpm 20
GM025
mPa.s
110 - 150
Monomer content
RS06C
%
41 - 46
Curing at 20°C with
0,3% Co6% + 1,5% MEKP
Gel time
RS08G
min.sec
11.00 - 15.00
Curing time
RS08G
min.sec
22.00 - 34.00
Maximum temperature
RS08G
°C
120 - 150
Properties of the liquid resin Distitron 429V1.3
Propiedades
Método de la prueba
Unidad de medida
Valor
Appearance - colour
RS13F
-----
Light yellow-green
Acid number
RS02C
mg KOH/g
13 - 20
Stability at 20°C in the dark
RS07G
months
6
Properties of cured unreinforced resin Distitron 429V1.3
Properties
Test method
Unit
Typical value
Tensile strength
ISO 527-1993
MPa
70
Tensile modulus
ISO 527-1993
MPa
3900
Elongation at break
ISO 527-1993
%
2,3
Flexural strength
ISO 178-2001
MPa
130
Flexural modulus
ISO 178-2001
MPa
4200
Heat deflection temperature
ISO 75 - 2:2004 Method A
°C
68
Glass transition
ASTM E 1545-00
°C
78
Barcol hardness at 25°C
ASTM D 2583-01
Unit
47
Full data sheet
Contact
Close
DISTITRON 454 V5
Delivery specification of the liquid resin Distitron 454V5
Properties
Test method
Unit
Typical value
Viscosity RVF at 25°C, s 2 rpm 20
GM025
mPa.s
460 - 570
Monomer content
RS06C
%
35 - 40
Curing at 25°C with
1% Co1% + 1% MEKP
Gel time
RS08G
min.sec
8.00 - 12.00
Curing time
RS08G
min.sec
17.00 - 28.00
Maximum temperature
RS08G
°C
170 - 200
Properties of the liquid resin Distitron 454V5
Properties
Test method
Unit
Typical value
Appearance - colour
RS13F
-----
Light yellow
Acid number
RS02C
mg KOH/g
20 - 27
Stability at 20°C in the dark
RS07G
months
6
Properties of cured unreinforced resin Distitron 454V5
Properties
Test method
Unit
Typical value
Tensile strength
ISO 527-1993
MPa
80
Tensile modulus
ISO 527-1993
MPa
3700
Elongation at break
ISO 527-1993
%
4,5
Flexural strength
ISO 178-2001
MPa
130
Flexural modulus
ISO 178-2001
MPa
3800
Heat deflection temperature
ISO 75 - 2:2004 Method A
°C
78
Barcol hardness at 25°C
ASTM D 2583-01
Unit
47
Full data sheet
Contact
Close
DISTITRON 514 AV2
Delivery specification of the liquid resin Distitron 514AV2
Properties
Test method
Unit
Typical value
Viscosity RVF at 25°C, s 2 rpm 20
GM025
mPa.s
280 - 370
Monomer content
RS06C
%
37 - 41
Curing at 25°C with
0,3% Co6% + 1% MEKP
Gel time
RS08G
min.sec
4.00 - 6.00
Curing time
RS08G
min.sec
10.00 - 18.00
Maximum temperature
RS08G
°C
165 - 195
Properties of the liquid resin Distitron 514AV2
Properties
Test method
Unit
Typical value
Appearance - colour
RS13F
-----
Light bluish
Acid number
RS02C
mg KOH/g
23 - 30
Stability at 20°C in the dark
RS07G
months
6
Delivery specification of the liquid resin Distitron 514AV2
Properties
Test method
Unit
Typical value
Tensile strength
ISO 527-1993
MPa
75
Tensile modulus
ISO 527-1993
MPa
4100
Elongation at break
ISO 527-1993
%
2,3
Flexural strength
ISO 178-2001
MPa
140
Flexural modulus
ISO 178-2001
MPa
4300
Heat deflection temperature
ISO 75 - 2:2004 Method A
°C
73
Glass transition
ASTM E 1545-00
°C
84
Barcol hardness at 25 °C
ASTM D 2583-87
Unit
48
Full data sheet
Contact
Close
DISTITRON 1402 LV4
Agreement of delivery specification of the liquid resin Distitron 1402LV4
Properties
Test method
Unit
Typical value
Viscosity RVF at 25 °C , s 2 rpm 20
GM025
mPa.s
340 - 410
Monomer content
RS06C
%
34 - 38
Curing at 25 °C with
0,25% Co6% + 1,5% MEKP
Gel time
RS08G
min.sec
21.00 - 27.00
Curing time
RS08G
min.sec
28.00 - 38.00
Maximum temperature
RS08G
°C
165 - 195
Properties of the liquid resin Distitron 1402LV4
Properties
Test method
Unit
Typical value
Appearance - colour
RS13F
-----
Light yellow
Acid number
RS02C
mg KOH/g
25 - 30
Stability at 20 °C in the dark
RS07G
months
6
Properties of cured unreinforced resin Distitron 1402LV4
Properties
Test method
Unit
Typical value
Tensile strength
ISO 527-1993
MPa
70
Tensile modulus
ISO 527-1993
MPa
4100
Elongation at break
ISO 527-1993
%
2,6
Flexural strength
ISO 178-2001
MPa
140
Flexural modulus
ISO 178-2001
MPa
4200
Heat deflection temperature
ISO 75/A
°C
78
Barcol hardness at 25 °C
ASTM D 2583-87
Unit
45
Full data sheet
Contact
Close
DISTITRON 1402 V4.5
Delivery specification of the liquid resin Distitron 1402V4.5
Properties
Test method
Unit
Typical value
Viscosity RVF at 25°C, s 2 rpm 20
GM025
mPa.s
380 - 470
Monomer content
RS06C
%
33 - 38
Curing at 20°C with
0,9% Co1% + 2% MEKP
Gel time
RS08G
min.sec
9.00 - 15.00
Curing time
RS08G
min.sec
15.00 - 27.00
Maximum temperature
RS08G
°C
170 - 195
Properties of the liquid resin Distitron 1402V4.5
Properties
Test method
Unit
Typical value
Appearance - colour
RS13F
-----
Light yellow
Acid number
RS02C
mg KOH/g
24 - 31
Stability at 20°C in the dark
RS07G
months
6
Properties of cured unreinforced resin Distitron 1402V4.5
Properties
Test method
Unit
Typical value
Tensile strength
ISO 527-1993
MPa
70
Tensile modulus
ISO 527-1993
MPa
4100
Elongation at break
ISO 527-1993
%
2,6
Flexural strength
ISO 178-2001
MPa
140
Flexural modulus
ISO 178-2001
MPa
4200
Heat deflection temperature
ISO 75 - 2:2004 Method A
°C
76
Barcol hardness at 25°C
ASTM D 2583-01
Unit
45
Full data sheet
Contact
Close
POLYNT 2482 TAE
Features of the liquid resin Polynt 2482 TAE
Properties
Test Method
Unit
Typical values
Specific weight at 20°C
g/cm³
1,11
Brookfield viscosity at 25°C, sp 2 rpm 20
MT-CUT25V
mPa.s
520 - 680
Solid content
MT-CU001C
%
58 - 62
Reactivity
a 25°C + 1% MEKP50
Gel time
RS.08.G
minutes
16 - 20
Delta
RS.08.G
minutes
9 - 16
Exothermic peak
RS.08.G
°C
115 - 140
Shelf life at 23°C in the dark
MT-CU002S
months
3
Properties of the cured unreinforced resin Polynt 2482 TAE
Properties
Test Method
Unit
Typical values
Curing cycle
24h at 23°C + 2h at 100°C + 1h at 100 ° C
Tensile strength
ISO 527 (2012)
MPa
50
Tensile modulus
ISO 527 (2012)
MPa
3900
Elongation at break
ISO 527 (2012)
%
1,5
Flexural strength
ISO 178/B (2010)
MPa
85
Flexural modulus
ISO 178/B (2010)
MPa
3900
HDT
ISO 75 -2A (2013)
°C
65
Glass transition
ASTM E 1545 (2011)
°C
78
Barcol hardness at 25°C
ASTM D 2583 (2007)
units
42
Full data sheet
Contact
Close
DISTITRON 3501 CV2.5
Delivery specification of the liquid resin Distitron 3501CV2.5
Properties
Test method
Unit
Value
Viscosity RVF at 25°C, s 2 rpm 20
GM025
mPa.s
210 - 290
Monomer content
RS06C
%
37 - 42
Curing at 25°C with
0,2% Co6% + 1,5% MEKP
Gel time
RS08G
min.sec
8.00 - 12.00
Curing time
RS08G
min.sec
19.00 - 28.00
Maximum temperature
RS08G
°C
140 - 170
Properties of the liquid resin Distitron 3501CV2.5
Properties
Test method
Unit
Value
Appearance - colour
RS13F
-----
Neutral
Acid number
RS02C
mg KOH/g
23 - 30
Stability at 20°C in the dark
RS07G
months
6
Properties of cured unreinforced resin Distitron 3501CV2.5
Properties
Test method
Unit
Typical value
Tensile strength
ISO 527-2012
MPa
67
Tensile modulus
ISO 527-2012
MPa
4100
Elongation at break
ISO 527-2012
%
2,0
Flexural strength
ISO 178-2010 Method B
MPa
110
Flexural modulus
ISO 178-2010 Method B
MPa
3900
Heat deflection temperature
ISO 75 - 2:2004 Method A
°C
55
Barcol hardness at 25°C
ASTM D 2583-07
Unit
44
Full data sheet
Contact
Close
DISTITRON 3501 CV4
Delivery specification of the liquid resin Distitron 3501CV4
Properties
Test method
Unit
Value
Viscosity RVF at 25°C, s 2 rpm 20
GM025
mPa.s
330 - 420
Monomer content
RS06C
%
35 - 39
Curing at 25°C with
0,6% Co6% + 2% MEKP
Gel time
RS08G
min.sec
5.00 - 8.00
Curing time
RS08G
min.sec
10.00 - 20.00
Maximum temperature
RS08G
°C
145 - 175
Properties of the liquid resin Distitron 3501CV4
Properties
Test method
Unit
Value
Appearance - colour
RS13F
-----
Neutral
Acid number
RS02C
mg KOH/g
24 - 31
Stability at 20°C in the dark
RS07G
months
6
Properties of cured unreinforced resin Distitron 3501CV4
Properties
Test method
Unit
Typical value
Tensile strength
ISO 527-1993
MPa
65
Tensile modulus
ISO 527-1993
MPa
4100
Elongation at break
ISO 527-1993
%
2,0
Flexural strength
ISO 178-2001
MPa
120
Flexural modulus
ISO 178-2001
MPa
4200
Heat deflection temperature
ISO 75 - 2:2004 Method A
°C
55
Barcol hardness at 25°C
ASTM D 2583-01
Unit
46
Full data sheet
Contact
Close
DISTITRON 3501 S
Delivery specification of the liquid resin Distitron 3501S
Properties
Test method
Unit
Value
Viscosity RVF at 25°C, s 2 rpm 20
GM025
mPa.s
330 - 420
Monomer content
RS06C
%
35 - 39
Curing at 25°C with
0,6% Co6% + 2% MEKP
Gel time
RS08G
min.sec
10.00 - 14.00
Curing time
RS08G
min.sec
22.00 - 32.00
Maximum temperature
RS08G
°C
140 - 170
Properties of the liquid resin Distitron 3501S
Properties
Test method
Unit
Value
Appearance - colour
RS13F
-----
Light violet
Acid number
RS02C
mg KOH/g
24 - 31
Stability at 20°C in the dark
RS07G
months
3
Properties of cured unreinforced resin Distitron 3501S
Properties
Test method
Unit
Typical value
Tensile strength
ISO 527-1993
MPa
65
Tensile modulus
ISO 527-1993
MPa
4000
Elongation at break
ISO 527-1993
%
2,0
Flexural strength
ISO 178-2001
MPa
110
Flexural modulus
ISO 178-2001
MPa
4200
Heat deflection temperature
ISO 75 - 2:2004 Method A
°C
54
Barcol hardness at 25°C
ASTM D 2583-01
Unit
46
Full data sheet
Contact
Close
DISTITRON 3519 AST
Delivery specification of the liquid resin Distitron 3519AST
Properties
Test method
Unit
Value
Viscosity RVF at 25°C, s 2 rpm 2
ISO 2555
mPa.s
2800 - 3200
Viscosity RVF at 25°C, s 2 rpm 20
ISO 2555
mPa.s
850 - 1050
Monomer content
RS06C
%
37 - 41
Curing at 25°C with
1,5% MEKP
Gel time
RS08G
min.sec
18.00 - 22.00
Curing time
RS08G
min.sec
38.00 - 47.00
Maximum temperature
RS08G
°C
130 - 140
Properties of the liquid resin Distitron 3519AST
Properties
Test method
Unit
Value
Appearance - colour
RS13F
-----
Opalescent rose
Acid number
RS02C
mg KOH/g
23 - 28
Stability at 20°C in the dark
RS07G
months
3
Properties of cured unreinforced resin Distitron 3519AST
Properties
Test method
Unit
Typical value
Tensile strength
ISO 527-1993
MPa
55
Tensile modulus
ISO 527-1993
MPa
4100
Elongation at break
ISO 527-1993
%
1,8
Flexural strength
ISO 178-1993
MPa
100
Flexural modulus
ISO 178-1993
MPa
4100
Heat deflection temperature
ISO 75/A
°C
67
Linear withdrawal after 24h at 25 ° C
ASTM D 2566-86
%
2,3
Barcol hardness at 25°C
ASTM D 2583-87
Unit
48
Full data sheet
Contact
Close
DISTITRON 3519 V2
Delivery specification of the liquid resin Distitron 3519V2
Properties
Test method
Unit
Value
Viscosity RVF at 25°C, s 2 rpm 20
GM025
mPa.s
170 - 250
Monomer content
RS06C
%
37 - 42
Curing at 25°C with
0,2% Co6% + 2% MEKP
Gel time
RS08G
min.sec
2.30 - 5.00
Curing time
RS08G
min.sec
7.00 - 15.00
Maximum temperature
RS08G
°C
175 - 200
Properties of the liquid resin Distitron 3519V2
Properties
Test method
Unit
Value
Appearance - colour
RS13F
-----
Light yellow
Stability at 20°C in the dark
RS07G
months
6
Properties of cured unreinforced resin Distitron 3519V2
Properties
Test method
Unit
Typical value
Tensile strength
ISO 527-2012
MPa
80
Tensile modulus
ISO 527-2012
MPa
4100
Elongation at break
ISO 527-2012
%
2,7
Flexural strength
ISO 178-2010 Method B
MPa
150
Flexural modulus
ISO 178-2010 Method B
MPa
4200
Heat deflection temperature
ISO 75 - 2:2013 Method A
°C
68
Barcol hardness at 25°C
ASTM D 2583-07
Unit
44
Full data sheet
Contact
Close
DISTITRON 3519 V13
Delivery specification of the liquid resin Distitron 3519V13
Properties
Test method
Unit
Typical value
Viscosity RVF at 25°C, s 3 rpm 20
GM025
mPa.s
1200 - 1500
Monomer content
RS06C
%
27 - 32
Curing at 25°C with
0,3% Co6% + 0,8% MEKP
Gel time
RS08G
min.sec
20.00 - 27.00
Curing time
RS08G
min.sec
31.00 - 41.00
Maximum temperature
RS08G
°C
145 - 175
Properties of the liquid resinDistitron 3519V13
Properties
Test method
Unit
Typical value
Appearance - colour
RS13F
-----
Light yellow
Acid number
RS02C
mg KOH/g
27 - 32
Stability at 20°C in the dark
RS07G
months
6
Properties of cured unreinforced resinDistitron 3519V13
Properties
Test method
Unit
Typical value
Tensile strength
ISO 527-1993
MPa
75
Tensile modulus
ISO 527-1993
MPa
4000
Elongation at break
ISO 527-1993
%
2,3
Flexural strength
ISO 178-2001
MPa
140
Flexural modulus
ISO 178-2001
MPa
4000
Heat deflection temperature
ISO 75 - 2:2004 Method A
°C
61
Barcol hardness at 25°C
ASTM D 2583-01
Unit
45
Full data sheet
Contact
Close
DISTITRON 5119
Delivery specification of the liquid resin Distitron 5119
Properties
Test method
Unit
Value
Viscosity RVF at 25°C, s 2 rpm 20
GM025
mPa.s
580 - 700
Monomer content
RS06C
%
31 - 35
Curing at 25°C with
0,3% Co6% + 0,8% MEKP
Gel time
RS08G
min.sec
20.00 - 27.00
Curing time
RS08G
min.sec
30.00 - 45.00
Maximum temperature
RS08G
°C
140 - 170
Properties of the liquid resin Distitron 5119
Properties
Test method
Unit
Value
Appearance - colour
RS13F
-----
Light yellow
Acid number
RS02C
mg KOH/g
24 - 31
Stability at 20°C in the dark
RS07G
months
5
Properties of cured unreinforced resin Distitron 5119
Properties
Test method
Unit
Typical value
Tensile strength
ISO 527-1993
MPa
70
Tensile modulus
ISO 527-1993
MPa
4000
Elongation at break
ISO 527-1993
%
2,3
Flexural strength
ISO 178-2001
MPa
130
Flexural modulus
ISO 178-2001
MPa
4100
Heat deflection temperature
ISO 75 - 2:2004 Method A
°C
62
Glass transition
ASTM E 1545-00
Unidad
66
Full data sheet
Contact
Close
DISTITRON 5119 E1SX20
Delivery specification of the liquid resin Distitron 5119E1SX20
Properties
Test method
Unit
Typical value
Viscosity RVF at 25°C, s 2 rpm 2
GM025
mPa.s
1800 - 2300
Viscosity RVF at 25°C, s 2 rpm 20
GM025
mPa.s
560 - 740
Monomer content
RS06C
%
38 - 43
Curing at 25°C with
0,8% MEKP
Gel time
RS08G
min.sec
12.00 - 17.00
Curing time
RS08G
min.sec
21.00 - 31.00
Maximum temperature
RS08G
°C
110 - 135
Properties of the liquid resin Distitron 5119E1SX20
Properties
Test method
Unit
Typical value
Appearance - colour
RS13F
-----
Opalescent orange
Acid number
RS02C
mg KOH/g
23 - 30
Stability at 20°C in the dark
RS07G
months
3
Properties of cured unreinforced resin Distitron 5119E1SX20
Properties
Test method
Unit
Typical value
Tensile strength
ISO 527-1993
MPa
50
Tensile modulus
ISO 527-1993
MPa
4000
Elongation at break
ISO 527-1993
%
1,6
Flexural strength
ISO 178-2001
MPa
90
Flexural modulus
ISO 178-2001
MPa
4100
Heat deflection temperature
ISO 75 - 2:2004 Method A
°C
64
Barcol hardness at 25°C
ASTM D 2583-01
Unit
45
Full data sheet
Contact
Close
DISTITRON 5119 E1SX20Q
Delivery specification of the liquid resin Distitron 5119E1SX20Q
Properties
Test method
Unit
Value
Viscosity RVF at 25°C, s 2 rpm 2
GM025
mPa.s
1600 - 2200
Viscosity RVF at 25°C, s 2 rpm 20
GM025
mPa.s
510 - 740
Monomer content
RS06C
%
39 - 44
Curing at 25°C with
1% MEKP
Gel time
RS08G
min.sec
11.00 - 15.00
Curing time
RS08G
min.sec
20.00 - 29.00
Maximum temperature
RS08G
°C
115 - 140
Properties of cured unreinforced resin Distitron 5119E1SX20Q
Properties
Test method
Unit
Value
Appearance - colour
RS13F
-----
Opalescent bluish
Stability at 20°C in the dark
RS07G
months
3
Properties of cured unreinforced resin Distitron 5119E1SX20Q
Properties
Test method
Unit
Typical value
Tensile strength
ISO 527-2012
MPa
50
Tensile modulus
ISO 527-2012
MPa
4000
Elongation at break
ISO 527-2012
%
1,4
Flexural strength
ISO 178-2010 Method B
MPa
85
Flexural modulus
ISO 178-2010 Method B
MPa
4000
Heat deflection temperature
ISO 75 - 2:2013 Method A
°C
64
Barcol hardness at 25°C
ASTM D 2583-07
Unidad
44
Full data sheet
Contact
Close
DISTITRON 5119 ELSXQ
Features of the liquid resin Distitron 5119ELSXQ
Properties
Test method
Unit
Typical values
Specific weight at 20°C
g/cm³
1,11
Brookfield viscosity at 25°C, sp 2 rpm 20
MT-CUT25V
mPa.s
670 - 830
Solid content
MT-CU001C
%
56 - 60
Reactivity
a 25°C + 1% MEKP50
Gel time
RS.08.G
minutes
16 - 20
Delta
RS.08.G
minutes
9 - 16
Exothermic peak
RS.08.G
°C
115 - 140
Shelf life at 23°C in the dark
MT-CU002S
meses
3
Properties of the cured unreinforced resin Distitron 5119ELSXQ
Properties
Test Method
Unit
Typical values
Curing cycle
24h at 23°C + 2h at 100°C + 1h at 100 ° C
Tensile strength
ISO 527 (2012)
MPa
50
Tensile modulus
ISO 527 (2012)
MPa
3900
Elongation at break
ISO 527 (2012)
%
1,5
Flexural strength
ISO 178/B (2010)
MPa
85
Flexural modulus
ISO 178/B (2010)
MPa
3900
HDT
ISO 75 -2A (2013)
°C
65
Glass transition
ASTM E 1545 (2011)
°C
78
Barcol hardness at 25°C
ASTM D 2583 (2007)
units
42
Full data sheet
Contact
Close
DISTITRON 5119 ESX20
Delivery specification of the liquid resin Distitron 5119ESX20
Properties
Test method
Unit
Typical value
Viscosity RVF at 25°C, s 2 rpm 2
GM025
mPa.s
1800 - 2300
Viscosity RVF at 25°C, s 2 rpm 20
GM025
mPa.s
560 - 740
Monomer content
RS06C
%
38 - 43
Curing at 25°C with
0,8% MEKP
Gel time
RS08G
min.sec
20.00 - 26.00
Curing time
RS08G
min.sec
29.00 - 40.00
Maximum temperature
RS08G
°C
110 - 135
Properties of the liquid resin Distitron 5119ESX20
Properties
Test method
Unit
Typical value
Appearance - colour
RS13F
-----
Opalescent orange
Acid number
RS02C
mg KOH/g
23 - 30
Stability at 20°C in the dark
RS07G
months
3
Properties of cured unreinforced resin Distitron 5119ESX20
Properties
Test method
Unit
Typical value
Tensile strength
ISO 527-1993
MPa
50
Tensile modulus
ISO 527-1993
MPa
4000
Elongation at break
ISO 527-1993
%
1,6
Flexural strength
ISO 178-2001
MPa
90
Flexural modulus
ISO 178-2001
MPa
4100
Heat deflection temperature
ISO 75 - 2:2004 Method A
°C
64
Barcol hardness at 25°C
ASTM D 2583-01
Unit
45
Full data sheet
Contact
Close
DISTITRON 5119 ESX20ZQ
Delivery specification of the liquid resin Distitron 5119ESX20ZQ
Properties
Test method
Unit
Value
Viscosity RVF at 25°C, s 2 rpm 2
GM025
mPa.s
1700 - 2100
Viscosity RVF at 25°C, s 2 rpm 20
GM025
mPa.s
520 - 680
Monomer content
RS06C
%
39 - 44
Curing at 25°C with
1% MEKP
Gel time
RS08G
min.sec
16.00 - 20.00
Curing time
RS08G
min.sec
25.00 - 36.00
Maximum temperature
RS08G
°C
115 - 140
Properties of the liquid resin Distitron 5119ESX20ZQ
Properties
Test method
Unit
Value
Appearance - colour
RS13F
-----
Opalescent bluish
Stability at 20°C in the dark
RS07G
months
3
Properties of cured unreinforced resin Distitron 5119ESX20ZQ
Properties
Test method
Unit
Typical value
Tensile strength
ISO 527-2012
MPa
45
Tensile modulus
ISO 527-2012
MPa
3900
Elongation at break
ISO 527-2012
%
1,4
Flexural strength
ISO 178-2010 Method B
MPa
80
Flexural modulus
ISO 178-2010 Method B
MPa
4000
Heat deflection temperature
ISO 75 - 2:2013 Method A
°C
61
Glass transition
ASTM E 1545-11
°C
75
Barcol hardness at 25°C
ASTM D 2583-07
Unit
45
Full data sheet
Contact
Close
DISTITRON 5119 S
Delivery specification of the liquid resin Distitron 5119S
Properties
Test method
Unit
Typical value
Viscosity RVF at 25°C, s 2 rpm 20
GM025
mPa.s
580 - 770
Monomer content
RS06C
%
31 - 35
Curing at 25°C with
0,8% MEKP
Gel time
RS08G
min.sec
21.00 - 27.00
Curing time
RS08G
min.sec
28.00 - 40.00
Maximum temperature
RS08G
°C
150 - 170
Properties of the liquid resin Distitron 5119S
Properties
Test method
Unit
Typical value
Appearance - colour
RS13F
-----
Rose-orange
Acid number
RS02C
mg KOH/g
24 - 31
Stability at 20°C in the dark
RS07G
months
4
Properties of cured unreinforced resin Distitron 5119S
Properties
Test method
Unit
Typical value
Tensile strength
ISO 527-1993
MPa
75
Tensile modulus
ISO 527-1993
MPa
4000
Elongation at break
ISO 527-1993
%
2,3
Flexural strength
ISO 178-2001
MPa
130
Flexural modulus
ISO 178-2001
MPa
4100
Heat deflection temperature
ISO 75 - 2:2004 Method A
°C
63
Glass transition
ASTM E 1545-00
°C
68
Full data sheet
Contact
Close
DISTITRON 5119 X
Delivery specification of the liquid resin Distitron 5119X
Properties
Test method
Unit
Typical value
Viscosity RVF at 25°C, s 2 rpm 2
GM025
mPa.s
1400 - 2000
Viscosity RVF at 25°C, s 2 rpm 20
GM025
mPa.s
420 - 630
Monomer content
RS06C
%
40 - 45
Curing at 25°C with
0,3% Co6% + 0,8% MEKP
Gel time
RS08G
min.sec
21.00 - 26.00
Curing time
RS08G
min.sec
36.00 - 47.00
Maximum temperature
RS08G
°C
145 - 175
Properties of the liquid resin Distitron 5119X
Properties
Test method
Unit
Typical value
Appearance - colour
RS13F
-----
Opalescent yellow
Acid number
RS02C
mg KOH/g
21 - 28
Stability at 20°C in the dark
RS07G
months
3
Properties of cured unreinforced resin Distitron 5119X
Properties
Test method
Unit
Typical value
Tensile strength
ISO 527-1993
MPa
50
Tensile modulus
ISO 527-1993
MPa
4100
Elongation at break
ISO 527-1993
%
1,6
Flexural strength
ISO 178-2001
MPa
90
Flexural modulus
ISO 178-2001
MPa
4200
Heat deflection temperature
ISO 75 - 2:2004 Method A
°C
65
Glass transition
ASTM E 1545-00
°C
73
Full data sheet
Contact
Close
Close
Special orthophthalic
DISTITRON 814 KV20
Delivery specification of the liquid resin Distitron 814KV20
Properties
Test method
Unit
Value
Viscosity RVF at 25°C, s 3 rpm 20
GM025
mPa.s
1700 - 2100
Monomer content
RS06C
%
30 - 34
Curing at 20°C with
3% PBO 50%
Gel time
RS08G
min.sec
8.30 - 10.30
Curing time
RS08G
min.sec
12.30 - 18.00
Maximum temperature
RS08G
°C
170 - 190
Properties of the liquid resin Distitron 814KV20
Properties
Test method
Unit
Value
Appearance - colour
RS13F
-----
Yellow
Acid number
RS02C
mg KOH/g
11 - 17
Stability at 20°C in the dark
RS07G
months
6
Properties of cured unreinforced resin Distitron 814KV20
Properties
Test method
Unit
Typical value
Tensile strength
ISO 527-2012
MPa
65
Tensile modulus
ISO 527-2012
MPa
3500
Elongation at break
ISO 527-2012
%
3,2
Flexural strength
ISO 178-2010 Method B
MPa
120
Flexural modulus
ISO 178-2010 Method B
MPa
3300
Heat deflection temperature
ISO 75 - 2:2004 Method A
°C
71
Barcol hardness at 25°C
ASTM D 2583-07
Unit
42
Full data sheet
Contact
Close
DISTITRON 1402 F
Delivery specification of the liquid resin Distitron 1402F
Properties
Test method
Unit
Value
ViscosityRVF a 25 °C , s 2 rpm 20
GM025
mPa.s
630 - 780
Monomer content
RS06C
%
31 - 35
Curing at 20°C with
0,9% Co1% + 2% MEKP
Gel time
RS08G
min.sec
9.00 - 15.00
Curing time
RS08G
min.sec
15.00 - 27.00
Maximum temperature
RS08G
°C
170 - 200
Properties of the liquid resin Distitron 1402F
Properties
Test method
Unit
Value
Appearance - colour
RS13F
-----
Light yellow
Acid number
RS02C
mg KOH/g
24 - 31
Stability at 20°C in the dark
RS07G
months
6
Properties of cured unreinforced resin Distitron 1402F
Properties
Test method
Unit
Typical value
Tensile strength
ISO 527-1993
MPa
80
Tensile modulus
ISO 527-1993
MPa
4100
Elongation at break
ISO 527-1993
%
2,8
Flexural strength
ISO 178-2001
MPa
140
Flexural modulus
ISO 178-2001
MPa
4200
Heat deflection temperature
ISO 75 - 2:2004 Method A
°C
73
Barcol hardness at 25°C
ASTM D 2583-01
Unit
45
Full data sheet
Contact
Close
Close
Isophthalic
DISTITRON 152 F
Delivery specification of the liquid resin Distitron 152F
Properties
Test method
Unit
Value
Viscosity RVF at 25°C, s 3 rpm 20
GM025
mPa.s
850 - 1150
Monomer content
RS06C
%
32 - 36
Curing at 25°C with
0.2% Co6% + 2% MEKP
Gel time
RS08G
min.sec
5.00 - 8.00
Curing time
RS08G
min.sec
11.00 - 18.00
Maximum temperature
RS08G
°C
180 - 210
Properties of the liquid resin Distitron 152F
Properties
Test method
Unit
Value
Appearance - colour
RS13F
-----
Light yellow
Acid number
RS02C
mg KOH/g
16 - 23
Stability at 20°C in the dark
RS07G
months
6
Properties of cured unreinforced resin Distitron 152F
Properties
Test method
Unit
Typical value
Tensile strength
ISO 527-1993
MPa
80
Tensile modulus
ISO 527-1993
MPa
3700
Elongation at break
ISO 527-1993
%
3.3
Flexural strength
ISO 178-2001
MPa
125
Flexural modulus
ISO 178-2001
MPa
3800
Heat deflection temperature
ISO 75 - 2:2004 Method A
°C
84
Glass transition
ASTM E 1545-00
°C
95
Barcol hardness at 25°C
ASTM D 2583-01
Unit
45
Full data sheet
Contact
Close
DISTITRON 183 B1
Delivery specification of the liquid resin Distitron 183B1
Properties
Test method
Unit
Value
Viscosity RVF at 25°C, s 3 rpm 20
GM025
mPa.s
900 - 1100
Monomer content
RS06C
%
33 - 37
Curing at 25°C with
0.3% Co6% + 1% MEKP
Gel time
RS08G
min.sec
12.00 - 16.00
Curing time
RS08G
min.sec
18.00 - 27.00
Maximum temperature
RS08G
°C
185 - 215
Properties of the liquid resin Distitron 183B1
Properties
Test method
Unit
Value
Appearance - colour
RS13F
-----
Light yellow
Acid number
RS02C
mg KOH/g
13 - 20
Stability at 20°C in the dark
RS07G
months
6
Properties of cured unreinforced resin Distitron 183B1
Properties
Test method
Unit
Typical value
Tensile strength
ISO 527-1993
MPa
80
Tensile modulus
ISO 527-1993
MPa
3500
Elongation at break
ISO 527-1993
%
4.0
Flexural strength
ISO 178-2001
MPa
130
Flexural modulus
ISO 178-2001
MPa
3400
Heat deflection temperature
ISO 75 - 2:2004 Method A
°C
94
Overall volume shrinkage
ISO 3521-1997 corr. 1:2003
%
8,3
Barcol hardness at 25°C
ASTM D 2583-01
Unit
42
Full data sheet
Contact
Close
DISTITRON 183 F
Copia de Especificaciones de la resina Distriton 183F líquida
Propiedades
Método de la prueba
Unidad de medida
Valor
Peso específico a 20°C
g/cm³
1,14
Viscosidad Brookfield a 25°C, eje 3 rpm 20
MT-CU025V
mPa.s
900 - 1100
Extracto seco
MT-CU001C
%
63 - 67
Reactividad
a 25°C + 0,3% Co 6% + 1%
MEKP50
Tiempo de gel
RS08G
min.sec
12 - 16
Delta
RS08G
min.sec
6 - 11
Temperatura de pico
RS08G
°C
185 - 215
Acidez
MT-CU001I
mgKOH/g
13 - 20
Estabilidad a 23°C en oscuridad
MT-CU002S
meses
4
Copia de Propiedades generales de la resina Distitron 183F líquida
Propiedades
Método de la prueba
Unidad de medida
Valor
Postcurado
24h a 23°C + 2h a 100°C + 1h a 100 ° C
Resistencia a tracción
ISO 527 (2012)
MPa
80
Módulo de tracción
ISO 527 (2012)
MPa
3500
Elongación a rotura
ISO 527 (2012)
%
4,3
Resistencia a flexión
ISO 178/B (2010)
MPa
140
Módulo de flexión
ISO 178/B (2010)
MPa
3400
HDT - Temperatura de flexión bajo carga
ISO 75 -2A (2013)
°C
94
Temperatura de transición vítrea
ASTM E 1545 (2011)
°C
103
Dureza Barcol a 25°C
ASTM D 2583 (2007)
Unidades
41
Full data sheet
Contact
Close
DISTITRON 195 A
Delivery specification of the liquid resin Distitron 195A
Properties
Test method
Unit
Value
Viscosity RVF at 25°C, s 3 rpm 20
GM025
mPa.s
620 - 780
Monomer content
RS06C
%
33 - 37
Curing at 25°C with
0,1% Co6% + 1% MEKP
Gel time
RS08G
min.sec
14,00 - 22,00
Curing time
RS08G
min.sec
23,00 - 37,00
Maximum temperature
RS08G
°C
165 - 195
Properties of the liquid resin Distitron 195A
Properties
Test method
Unit
Value
Appearance - colour
RS13F
-----
Light yellow
Acid number
RS02C
mg KOH/g
6 - 13
Stability at 20°C in the dark
RS07G
months
6
Properties of cured unreinforced resin Distitron 195A
Properties
Test method
Unit
Typical value
Tensile strength
ISO 527-1993
MPa
65
Tensile modulus
ISO 527-1993
MPa
3100
Elongation at break
ISO 527-1993
%
7,3
Creep tension
ISO 527-1993
MPa
65
Creep deformation
ISO 527-1993
%
4,3
Flexural strength
ISO 178-2001
MPa
110
Flexural modulus
ISO 178-2001
MPa
3200
Heat deflection temperature
ISO 75 - 2:2004 Method A
°C
64
Overall volume shrinkage
ASTM E 1545-00
°C
76
Barcol hardness at 25°C
ASTM D 2583-01
Unidad
32
Full data sheet
Contact
Close
DISTITRON 1629
Delivery specification of the liquid resin Distitron 1629
Properties
Test method
Unit
Value
Viscosity RVF at 25°C, s 2 rpm 20
GM025
mPa.s
260 - 340
Monomer content
RS06C
%
38 - 43
Curing at 25°C with
0.3% Co6% + 1% MEKP
Gel time
RS08G
min.sec
7.00 - 11.00
Curing time
RS08G
min.sec
14.00 - 23.00
Maximum temperature
RS08G
°C
190 - 220
Properties of the liquid resin Distitron 1629
Properties
Test method
Unit
Value
Appearance - colour
RS13F
-----
Light yellow
Acid number
RS02C
mg KOH/g
11 - 18
Stability at 20°C in the dark
RS07G
months
6
Properties of cured unreinforced resin Distitron 1629
Properties
Test method
Unit
Typical value
Tensile strength
ISO 527-2012
MPa
80
Tensile modulus
ISO 527-2012
MPa
3800
Elongation at break
ISO 527-2012
%
2.8
Flexural strength
ISO 178-2010 Method B
MPa
135
Flexural modulus
ISO 178-2010 Method B
MPa
3900
Heat deflection temperature
ISO 75 - 2:2004 Method A
°C
105
Glass transition
ASTM E 1545-11
°C
113
Barcol hardness at 25°C
ASTM D 2583-07
Unit
41
Full data sheet
Contact
Close
DISTITRON 1629 CV8
Delivery specification of the liquid resin Distitron 1629CV8
Properties
Test method
Unit
Value
Viscosity RVF at 25°C, s 2 rpm 20
GM025
mPa.s
720 - 880
Monomer content
RS06C
%
34 - 39
Curing SPI at 82.2°C with
2% PBO 50%
SPI
RS03G
min.sec
7.00 - 8.00
LPE
RS03G
min.sec
8.00 - 11.00
MTE
RS03G
°C
205 - 235
Properties of the liquid resin Distitron 1629CV8
Properties
Test method
Unit
Value
Appearance - colour
RS13F
-----
Light yellow
Acid number
RS02C
mg KOH/g
15 - 21
Stability at 20°C in the dark
RS07G
months
6
Properties of cured unreinforced resin Distitron 1629CV8
Properties
Test method
Unit
Typical value
Tensile strength
ISO 527-1993
MPa
70
Tensile modulus
ISO 527-1993
MPa
3800
Elongation at break
ISO 527-1993
%
2.5
Flexural strength
ISO 178-2001
MPa
130
Flexural modulus
ISO 178-2001
MPa
3800
Heat deflection temperature
ISO 75 - 2:2004 Method A
°C
95
Glass transition
ASTM E 1545-00
°C
115
Barcol hardness at 25°C
ASTM D 2583-01
Unit
47
Full data sheet
Contact
Close
DISTITRON 1629 FNT
Delivery specification of the liquid resin 1629FNT
Properties
Test method
Unit
Value
Viscosity RVF at 25°C, s 2 rpm 2
GM025
mPa.s
1400 - 2000
Viscosity RVF at 25°C, s 2 rpm 20
GM025
mPa.s
460 - 700
Monomer content
RS06C
%
42 - 47
Curing at 25°C with
2% MEKP
Gel time
RS08G
min.sec
5,00 - 8,30
Curing time
RS08G
min.sec
12,00 - 20,00
Maximum temperature
RS08G
°C
190 - 220
Properties of the liquid resin Distitron 1629FNT
Properties
Test method
Unit
Value
Appearance - colour
RS13F
-----
Opalescent rose
Stability at 20°C in the dark
RS07G
months
3
Properties of cured unreinforced resin 1629FNT
Properties
Test method
Unit
Typical value
Tensile strength
ISO 527-1993
MPa
55
Tensile modulus
ISO 527-1993
MPa
3800
Elongation at break
ISO 527-1993
%
1,9
Flexural strength
ISO 178-2001
MPa
100
Flexural modulus
ISO 178-2001
MPa
4000
Heat deflection temperature
ISO 75 - 2:2004 Method A
°C
103
Glass transition
ASTM E 1545-00
°C
112
Barcol hardness at 25°C
ASTM D 2583-01
Unit
48
Full data sheet
Contact
Close
DISTITRON 1629 LV12
Delivery specification of the liquid resin Distitron 1629LV12
Properties
Test method
Unit
Typical value
Viscosity RVF at 25°C, s 3 rpm 20
GM025
mPa.s
1200 - 1450
Monomer content
RS06C
%
31 - 36
Curing at 25°C with
0.3% Co6% + 1% MEKP
Gel time
RS08G
min.sec
19.00 - 25.00
Curing time
RS08G
min.sec
24.00 - 36.00
Maximum temperature
RS08G
°C
180 - 210
Properties of the liquid resin Distitron 1629LV12
Properties
Test method
Unit
Typical value
Appearance - colour
RS13F
-----
Light yellow
Acid number
RS02C
mg KOH/g
15 - 20
Stability at 20°C in the dark
RS07G
months
6
Properties of cured unreinforced resin Distitron 1629LV12
Properties
Test method
Unit
Typical value
Tensile strength
ISO 527-1993
MPa
70
Tensile modulus
ISO 527-1993
MPa
4000
Elongation at break
ISO 527-1993
%
2.0
Flexural strength
ISO 178-2001
MPa
140
Flexural modulus
ISO 178-2001
MPa
3900
Heat deflection temperature
ISO 75 - 2:2004 Method A
°C
97
Glass transition
ASTM E 1545-00
°C
112
Barcol hardness at 25°C
ASTM D 2583-01
Unit
49
Full data sheet
Contact
Close
DISTITRON 1629 NT
Properties of cured unreinforced resin Distitron 1629NT
Properties
Test method
Unit
Typical value
Viscosity RVF at 25°C, s 2 rpm 2
GM025
mPa.s
1400 - 2000
Viscosity RVF at 25°C, s 2 rpm 20
GM025
mPa.s
450 - 700
Monomer content
RS06C
%
42 - 47
Curing at 25°C with
2% MEKP
Gel time
RS08G
min.sec
5,00 - 8,00
Curing time
RS08G
min.sec
12,00 - 19,00
Maximum temperature
RS08G
°C
190 - 220
Properties of the liquid resin Distitron 1629NT
Properties
Test method
Unit
Value
Appearance - colour
RS13F
-----
Opalescent rose
Stability at 20°C in the dark
Estabilidad a 20°C en la oscuridad
RS07G
months
3
Properties of cured unreinforced resin Distitron 1629NT
Properties
Test method
Unit
Typical value
Tensile strength
ISO 527-2012
MPa
50
Tensile modulus
ISO 527-2012
MPa
3800
Elongation at break
ISO 527-2012
%
1,5
Flexural strength
ISO 178-2010 Method B
MPa
100
Flexural modulus
ISO 178-2010 Method B
MPa
3900
Heat deflection temperature
ISO 75 - 2:2004 Method A
°C
103
Glass transition
ASTM E 1545-11
°C
112
Barcol hardness at 25°C
ASTM D 2583-07
Unit
46
Full data sheet
Contact
Close
DISTITRON 1629 T
Delivery specification of the liquid resin Distitron 1629T
Properties
Test method
Unit
Value
Viscosity RVF at 25°C, s 2 rpm 2
GM025
mPa.s
1600 - 2000
Viscosity RVF at 25°C, s 2 rpm 20
GM025
mPa.s
530 - 680
Monomer content
RS06C
%
41 - 46
Curing at 25°C with
0,6% Co6% + 2% MEKP
Gel time
RS08G
min.sec
5,00 - 8,00
Curing time
RS08G
min.sec
10,00 - 17,00
Maximum temperature
RS08G
°C
185 - 215
Properties of the liquid resin Distitron 1629T
Properties
Test method
Unit
Value
Appearance - colour
RS13F
-----
Opalescent yellow
Stability at 20°C in the dark
RS07G
months
3
Properties of cured unreinforced resin Distitron 1629T
Properties
Test method
Unit
Typical value
Tensile strength
ISO 527-1993
MPa
55
Tensile modulus
ISO 527-1993
MPa
3800
Elongation at break
ISO 527-1993
%
1,9
Flexural strength
ISO 178-2001
MPa
100
Flexural modulus
ISO 178-2001
MPa
4000
Heat deflection temperature
ISO 75 - 2:2004 Method A
°C
103
Glass transition
ASTM E 1545-00
°C
112
Barcol hardness at 25°C
ASTM D 2583-01
Unit
48
Full data sheet
Contact
Close
DISTITRON 1629 XYQ
Delivery specification of the liquid resin Distitron 1629XYQ
Properties
Test method
Unit
Value
Viscosity RVF at 25°C, s 2 rpm 2
GM025
mPa.s
1400 - 2000
Viscosity RVF at 25°C, s 2 rpm 20
GM025
mPa.s
450 - 700
Monomer content
RS06C
%
42 - 47
Curing at 25°C with
1% MEKP
Gel time
RS08G
min.sec
26.00 - 35.00
Curing time
RS08G
min.sec
48.00 - 65.00
Maximum temperature
RS08G
°C
155 - 185
Properties of the liquid resin Distitron 1629XYQ
Properties
Test method
Unit
Value
Appearance - colour
RS13F
-----
Opalescent bluish
Stability at 20°C in the dark
RS07G
months
3
Properties of cured unreinforced resin Distitron 1629XYQ
Properties
Test method
Unit
Typical value
Tensile strength
ISO 527-1993
MPa
55
Tensile modulus
ISO 527-1993
MPa
3800
Elongation at break
ISO 527-1993
%
1,7
Flexural strength
ISO 178-2001
MPa
100
Flexural modulus
ISO 178-2001
MPa
3900
Heat deflection temperature
ISO 75 - 2:2004 Method A
°C
103
Glass transition
ASTM E 1545-00
°C
112
Barcol hardness at 25°C
ASTM D 2583-01
Unit
47
Full data sheet
Contact
Close
POLYNT 3201 TAQ3
Copia de Características de la resina líquida POLYNT 3201 TAQ3
Propiedades
Método de ensayo
Unidad de medida
Valores típicos
Peso específico a 20°C
g/cm³
1,12
Viscosidad Brookfield a 25°C, eje 2 rpm 20
MT-CUT23V
mPa.s
700 - 900
Extracto seco
MT-CU001C
%
55 - 59
Reactividad
a 23°C + 1,5% MEKP50
Tiempo de gel
MT-CU151R
minutos
34 - 40
Delta
MT-CU151R
minutos
65 - 75
Temperatura de pico
MT-CU151R
°C
60 - 80
Estabilidad a 23°C en oscuridad
MT-CU002S
minutos
6
Copia de Propiedades de la resina líquida POLYNT 3201 TAQ3
Propiedades
Método de ensayo
Unidad de medida
Valores típicos
Postcurado
24h a 23°C + 2h a 100°C + 1h a 100 ° C
Resistencia a tracción
ISO 527 (2012)
MPa
46
Módulo de tracción
ISO 527 (2012)
MPa
3356
Elongación a rotura
ISO 527 (2012)
%
1,53
Resistencia a flexión
ISO 178 (2011)
MPa
81
Módulo de flexión
ISO 178 (2011)
MPa
3191
HDT - Temperatura de flexión bajo carga
ISO 75 -2A (2013)
°C
68
Full data sheet
Contact
Close
Close
Infusion and RTM
152S1
Delivery specification of the liquid resin Distitron 152S1
Properties
Test method
Unit
Value
Viscosity RVF a 25 °C , s 2 rpm 20
GM025
mPa.s
180 - 270
Monomers content
RS06C
%
39 - 44
Curing at 20°C with
1% MEKP
Gel time
RS08G
min.sec
90,00 - 110,00
Curing time
RS08G
min.sec
135,00 - 175,00
Maximum temperature
RS08G
°C
110 - 135
Properties of the liquid resin Distitron 152S1
Properties
Test method
Unit
Value
Appearance - colour
RS13F
-----
Gray - Purple
Acid number
RS02C
mg KOH/g
14 - 21
Stability at 20°C in the dark
RS07G
months
3
Properties of cured unreinforced resin Distitron 152S1
Properties
Test method
Unit
Typical value
Tensile strength
ISO 527-1993
MPa
80
Tensile modulus
ISO 527-1993
MPa
3600
Elongation at break
ISO 527-1993
%
3,1
Flexural strength
ISO 178-2001
MPa
130
Flexural modulus
ISO 178-2001
MPa
3700
Glass transition
RS09M
°C
108
Heat deflection temperature
ISO 75 - 2:2004 Method A
°C
98
Overall volume shrinkage
ISO 3521-1997 corr. 1:2003
%
8,5
Barcol hardness at 25°C
ASTM D 2583-87
Unit
45
Full data sheet
Contact
Close
152SC
Delivery specification of the liquid resin Distitron 152SC
Properties
Test method
Unit
Value
Viscosity RVF at 25°C, s 2 rpm 20
GM025
mPa.s
180 - 270
Monomer content
RS06C
%
39 - 44
Curing at 20°C with
1,5% MEKP
Gel time
RS08G
min.sec
80,00 - 95,00
Curing time
RS08G
min.sec
110,00 - 140,00
Maximum temperature
RS08G
°C
140 - 165
Properties of the liquid resin Distitron 152SC
Properties
Test method
Unit
Value
Appearance ‐ colour
RS13F
-----
Rose ‐ violet
Acid number
RS02C
mg KOH/g
14 - 21
Stability at 20°C in the dark
RS07G
months
3
Properties of cured unreinforced resin Distitron 152SC
Properties
Test method
Unit
Typical value
Tensile strength
ISO 527‐2012
MPa
75
Tensile modulus
ISO 527‐2012
MPa
3500
Elongation at break
ISO 527‐2012
%
3,2
Flexural strength
IISO 178‐2010 Method B
MPa
135
Flexural modulus
ISO 178‐2010 Method B
MPa
3400
Glass transition
ASTM E 1545‐11
°C
107
Heat deflection temperature
ISO 75 ‐ 2:2013 Method A
°C
95
Overall volume shrinkage
ISO 3521-1997 corr. 1:2003
%
8,4
Barcol hardness at 25°C
ASTM D 2583-07
Unit
43
Full data sheet
Contact
Close
429SV1,3
Delivery specification of the liquid resin Distitron 429SV1.3
Properties
Test method
Unit
Typical value
Viscosity RVF at 25°C, s 2 rpm 20
GM025
mPa.s
110 - 150
Monomer content
RS06C
%
41 - 45
Curing at 20°C with
1,5% MEKP (on 50g of resin)
Gel time
RS08G
min.sec
9.00 - 12.00
Curing time
RS08G
min.sec
20.00 - 31.00
Maximum temperature
RS08G
°C
115 - 145
Properties of the liquid resin Distitron 429SV1.3
Properties
Test method
Unit
Typical value
Appearance - colour
RS13F
-----
Rose
Acid number
RS02C
mg KOH/g
13 - 20
Stability at 20°C in the dark
RS07G
months
6
Properties of cured unreinforced resin Distitron 429SV1.3
Properties
Test method
Unit
Typical value
Tensile strength
ISO 527-1993
MPa
70
Tensile modulus
ISO 527-1993
MPa
3900
Elongation at break
ISO 527-1993
%
2,3
Flexural strength
ISO 178-1993
MPa
130
Flexural modulus
ISO 178-1993
MPa
4200
Glass transition
ASTM E 1545-00
°C
78
Heat deflection temperature
ISO 75 - 2:2004 Method A
°C
68
Barcol hardness at 25°C
ASTM D 2583-01
Unit
47
Full data sheet
Contact
Close
429V1,3
Delivery specification of the liquid resin Distitron 429V1.3
Properties
Test method
Unit
Value
Viscosity RVF at 25°C, s 2 rpm 20
GM025
mPa.s
110 - 150
Monomer content
RS06C
%
41 - 46
Curing at 20°C with
0,3% Co6% - 1,5% MEKP (on 50g of resin)
Gel time
RS08G
min.sec
11.00 - 15.00
Curing time
RS08G
min.sec
24.00 - 34.00
Maximum temperature
RS08G
°C
115 - 145
Properties of the liquid resin Distitron 429V1.3
Properties
Test method
Unit
Value
Appearance - colour
RS13F
-----
Light yellow-green
Stability at 20°C in the dark
RS07G
months
6
Properties of cured unreinforced resin Distitron 429V1.3
Properties
Test method
Unit
Typical value
Tensile strength
ISO 527-1993
MPa
70
Tensile modulus
ISO 527-1993
MPa
3900
Elongation at break
ISO 527-1993
%
2,3
Flexural strength
ISO 178-2001
MPa
130
Flexural modulus
ISO 178-2001
MPa
4200
Glass transition
ASTM E 1545-00
°C
78
Heat deflection temperature
ISO 75 - 2:2004 Method A
°C
68
Barcol hardness at 25°C
ASTM D 2583-01
Unit
47
Full data sheet
Contact
Close
I100SV1,5
Delivery specification of the liquid resin Distitron I100SV1,5
Properties
Test method
Unit
Value
Viscosity RVF at 25°C, s 2 rpm 20
GM025
mPa.s
120 - 160
Monomer content
RS06C
%
35 - 40
Curing at 20°C with
1,5% MEKP
Gel time
RS08G
min.sec
58.00 - 68.00
Curing time
RS08G
min.sec
76.00 - 96.00
Maximum temperature
RS08G
°C
135 - 165
Properties of the liquid resin Distitron I100SV1,5
Properties
Test method
Unit
Value
Appearance - colour
RS13F
-----
Orange rose
Stability at 20°C in the dark
RS07G
motnhs
3
Properties of cured unreinforced resin Distitron I100SV1,5
Properties
Test method
Unit
Typical value
Tensile strength
ISO 527-1993
MPa
75
Tensile modulus
ISO 527-1993
MPa
3500
Elongation at break
ISO 527-1993
%
3,8
Flexural strength
ISO 178-2001
MPa
130
Flexural modulus
ISO 178-2001
MPa
3500
Heat deflection temperature
ISO 75 - 2:2004 Method A
°C
79
Barcol hardness at 25°C
ASTM D 2583-01
Unit
42
Full data sheet
Contact
Close
VE370SCD
Delivery specification of the liquid resin Distitron VE370SCD
Properties
Test method
Unit
Value
Viscosity RVF at 25°C, s 2 rpm 20
GM025
mPa.s
120 - 140
Monomer content
RS06C
%
44 - 49
Curing at 20°C with
0,3% Co6% + 1,5% Cumyl hydroperoxide
Gel time
RS08G
min.sec
95.00 - 115.00
Curing time
RS08G
min.sec
135.00 - 175.00
Maximum temperature
RS08G
°C
120 - 150
Properties of the liquid resin Distitron VE370SCD
Properties
Test method
Unit
Value
Appearance - colour
RS13F
-----
Yellow brown
Acid number
RS02C
mg KOH/g
<10
Stability at 20°C in the dark
RS07G
months
4
Properties of cured unreinforced resin Distitron VE370SCD
Properties
Test method
Unit
Typical value
Tensile strength
ISO 527-1993
MPa
85
Tensile modulus
ISO 527-1993
MPa
3500
Elongation at break
ISO 527-1993
%
6,6
Stress at yield
ISO 527-1993
MPa
85
Strain at yield
ISO 527-1993
%
5,0
Flexural strength
ISO 178-2001
MPa
145
Flexural modulus
ISO 178-2001
MPa
3600
Heat deflection temperature
ISO 75 - 2:2004 Method A
°C
108
Glass transition
ASTM E 1545-00
°C
115
Barcol hardness at 25°C
ASTM D 2583-01
Unit
40
Full data sheet
Contact
Close
Close
NPG isophthalic
DISTITRON 152
Delivery specification of the liquid resin Distitron 152
Properties
Test method
Unit
Typical value
Viscosity RVF at 25°C, s 3 rpm 20
GM025
mPa.s
850 - 1150
Monomer content
RS06C
%
32 - 37
Reactividad a 25°C con
0.2% Co6% + 2% MEKP
Gel time
RS08G
min.sec
5.30 - 7.30
Curing time
RS08G
min.sec
11.00 - 17.00
Maximum temperature
RS08G
°C
180 - 210
Properties of the liquid resin Distitron 152
Properties
Test method
Unit
Typical value
Appearance - colour
RS13F
-----
Light yellow
Acid number
RS02C
mg KOH/g
16 - 23
Stability at 20°C in the dark
RS07G
months
6
Properties of cured unreinforced resin Distitron 152
Properties
Test method
Unit
Typical value
Tensile strength
ISO 527-1993
MPa
80
Tensile modulus
ISO 527-1993
MPa
3700
Elongation at break
ISO 527-1993
%
3.3
Flexural strength
ISO 178-2001
MPa
125
Flexural modulus
ISO 178-2001
MPa
3800
Heat deflection temperature
ISO 75 - 2:2004 Method A
°C
84
Glass transition
ASTM E 1545-00
°C
95
Barcol hardness at 25°C
ASTM D 2583-01
Unit
45
Full data sheet
Contact
Close
DISTITRON 152 X
Delivery specification of the liquid resin Distitron 152X
Properties
Test method
Unit
Typical value
Viscosity RVF a 25 °C , s 2 rpm 2
GM025
mPa.s
1400 - 2100
Viscosity RVF a 25 °C , s 2 rpm 20
GM025
mPa.s
460 - 740
Monomer content
RS06C
%
39 - 44
Curing at 25°C with
0,2% Co6% + 1,5% MEKP
Gel time
RS08G
min.sec
16.00 - 21.00
Curing time
RS08G
min.sec
26.00 - 37.00
Maximum temperature
RS08G
°C
170 - 200
Properties of the liquid resin Distitron 152X
Properties
Test method
Unit
Typical value
Appearance - colour
RS13F
-----
Opalescent yellow
Acid number
RS02C
mg KOH/g
13 - 20
Stability at 20°C in the dark
RS07G
months
3
Properties of cured unreinforced resin Distitron 152X
Properties
Test method
Unit
Typical value
Tensile strength
ISO 527-1993
MPa
60
Tensile modulus
ISO 527-1993
MPa
3600
Elongation at break
ISO 527-1993
%
1,9
Flexural strength
ISO 178-2001
MPa
100
Flexural modulus
ISO 178-2001
MPa
3700
Heat deflection temperature
ISO 75 - 2:2004 Method
°C
102
Glass transition
ASTM E 1545-00
°C
114
Barcol hardness at 25°C
ASTM D 2583-87
Unidad
42
Full data sheet
Contact
Close
Close
DCPD
DISTITRON 100 BSX15
Delivery specification of the liquid resin Distitron 100BSX15
Properties
Test method
Unit
Value
Viscosity RVF at 25°C, s 2 rpm 2
GM025
mPa.s
1400 - 2000
Viscosity RVF at 25°C, s 2 rpm 20
GM025
mPa.s
460 - 670
Monomer content
RS06C
%
40 - 41
Curing at 20°C with
1.5% MEKP
Gel time
RS08G
min.sec
18.00 - 26.00
Curing time
RS08G
min.sec
35.00 - 50.00
Maximum temperature
RS08G
°C
130 - 160
Properties of the liquid resin Distitron 100BSX15
Properties
Test method
Unit
Value
Appearance - colour
RS13F
-----
Opalescent bluish
Stability at 20°C in the dark
RS07G
months
3
Properties of cured unreinforced resin Distitron 100BSX15
Properties
Test method
Unit
Typical value
Tensile strength
ISO 527-1993
MPa
45
Tensile modulus
ISO 527-1993
MPa
3500
Elongation at break
ISO 527-1993
%
1.4
Flexural strength
ISO 178-2001
MPa
90
Flexural modulus
ISO 178-2001
MPa
3600
Heat deflection temperature
ISO 75 - 2:2004 Method A
°C
82
Glass transition
ASTM E 1545-00
°C
100
Barcol hardness at 25°C
ASTM D 2583-01
Unit
42
Full data sheet
Contact
Close
DISTITRON 100 BX15
Delivery specification of the liquid resin Distitron 100BX15
Properties
Test method
Unit
Value
Viscosity RVF at 25°C, s 2 rpm 2
GM025
mPa.s
1400 - 2000
Viscosity RVF at 25°C, s 2 rpm 20
GM025
mPa.s
470 - 650
Monomer content
RS06C
%
40 - 41
Curing at 20°C with
0,35% Co6% + 1,5% MEKP
Gel time
RS08G
min.sec
18.00 - 26.00
Curing time
RS08G
min.sec
35.00 - 50.00
Maximum temperature
RS08G
°C
130 - 160
Properties of the liquid resin Distitron 100BX15
Propiedades
Método de la prueba
Unidad de medida
Valor
Appearance - colour
RS13F
-----
Opalescente bluish
Stability at 20°C in the dark
RS07G
months
3
Properties of cured unreinforced resin Distitron 100BX15
Properties
Test method
Unit
Typical value
Tensile strength
ISO 527-1993
MPa
45
Tensile modulus
ISO 527-1993
MPa
3500
Elongation at break
ISO 527-1993
%
1.4
Flexural strength
ISO 178-2001
MPa
90
Flexural modulus
ISO 178-2001
MPa
3600
Heat deflection temperature
ISO 75 - 2:2004 Method A
°C
82
Glass transition
ASTM E 1545-00
°C
100
Barcol hardness at 25°C
ASTM D 2583-01
Unit
42
Full data sheet
Contact
Close
DISTITRON 100 DSX15
Delivery specification of the liquid resin Distitron 100DSX15
Properties
Test method
Unit
Typical value
Viscosity RVF at 25°C, s 2 rpm 2
GM025
mPa.s
1600 - 2000
Viscosity RVF at 25°C, s 2 rpm 20
GM025
mPa.s
470 - 670
Monomer content
RS06C
%
40 - 41
Curing at 25°C with
1.5% MEKP
Gel time
RS08G
min.sec
19.00 - 25.00
Curing time
RS08G
min.sec
36.00 - 48.00
Maximum temperature
RS08G
°C
135 - 165
Properties of the liquid resin Distitron 100DSX15
Properties
Test method
Unit
Typical value
Appearance - colour
RS13F
-----
Opalescent bluish
Stability at 20°C in the dark
RS07G
months
3
Properties of cured unreinforced resin Distitron 100DSX15
Properties
Test method
Unit
Typical value
Tensile strength
ISO 527-1993
MPa
50
Tensile modulus
ISO 527-1993
MPa
3600
Elongation at break
ISO 527-1993
%
1.5
Flexural strength
ISO 178-2001
MPa
85
Flexural modulus
ISO 178-2001
MPa
3800
Heat deflection temperature
ISO 75 - 2:2004 Method A
°C
79
Glass transition
ASTM E 1545-00
°C
96
Barcol hardness at 25°C
ASTM D 2583-01
Unit
43
Full data sheet
Contact
Close
DISTITRON 100 V9
Delivery specification of the liquid resin Distitron 100V9
Properties
Test method
Unit
Value
Viscosity RVF at 25°C, s 3 rpm 20
GM025
mPa.s
870 - 1050
Monomer content
RS06C
%
25 - 29
Curing at 25°C with
0.4% Co6% + 2% CHP
Gel time
RS08G
min.sec
5.00 - 6.30
Curing time
RS08G
min.sec
9.00 - 14.00
Maximum temperature
RS08G
°C
135 - 165
Properties of the liquid resin Distitron 100V9
Properties
Test method
Unit
Value
Appearance - colour
RS13F
-----
Yellow
Stability at 20°C in the dark
RS07G
months
3
Properties of cured unreinforced resin Distitron 100V9
Properties
Test method
Unit
Typical value
Tensile strength
ISO 527-1993
MPa
63
Tensile modulus
ISO 527-1993
MPa
2900
Elongation at break
ISO 527-1993
%
4.2
Flexural strength
ISO 178-2001
MPa
105
Flexural modulus
ISO 178-2001
MPa
2900
Heat deflection temper
ISO 75 - 2:2004 Method A
°C
58
Barcol hardness at 25°C
ASTM D 2583-01
Unit
37
Full data sheet
Contact
Close
DISTITRON 100 X15
Delivery specification of the liquid resin Distitron 100X15
Properties
Test method
Unit
Typical value
Viscosity RVF at 25°C, s 2 rpm 2
GM025
mPa.s
1600 - 2000
Viscosity RVF at 25°C, s 2 rpm 20
GM025
mPa.s
420 - 630
Monomer content
RS06C
%
40 - 41
Curing at 25°C with
0.35% Co6% + 1.5% MEKP
Gel time
RS08G
min.sec
19.00 - 25.00
Curing time
RS08G
min.sec
36.00 - 48.00
Maximum temperature
RS08G
°C
135 - 165
Properties of the liquid resin Distitron 100X15
Properties
Test method
Unit
Typical value
Appearance - colour
RS13F
-----
Opalescent bluish
Acid number
RS02C
mg KOH/g
16 - 23
Stability at 20°C in the dark
RS07G
months
3
Properties of cured unreinforced resin Distitron 100X15
Properties
Test method
Unit
Typical value
Tensile strength
ISO 527-1993
MPa
45
Tensile modulus
ISO 527-1993
MPa
3500
Elongation at break
ISO 527-1993
%
1.4
Flexural strength
ISO 178-2001
MPa
90
Flexural modulus
ISO 178-2001
MPa
3600
Heat deflection temperature
ISO 75 - 2:2004 Method A
°C
82
Glass transition
ASTM E 1545-00
°C
100
Barcol hardness at 25°C
ASTM D 2583-01
Unit
42
Full data sheet
Contact
Close
DISTITRON 110 BX
Delivery specification of the liquid resin Distitron 110BX
Properties
Test method
Unit
Value
Viscosity RVF at 25°C, s 2 rpm 2
GM025
mPa.s
750 - 1000
Viscosity RVF at 25°C, s 2 rpm 20
GM025
mPa.s
180 - 320
Monomer content
RS06C
%
40 - 44
Curing at 25°C with
0.35% Co6% + 1.5% MEKP
Gel time
RS08G
min.sec
11.00 - 15.00
Curing time
RS08G
min.sec
21.00 - 31.00
Maximum temperature
RS08G
°C
165 - 195
Properties of the liquid resin Distitron 110BX
Properties
Test method
Unit
Value
Appearance - colour
RS13F
-----
Opalescent bluish
Stability at 20°C in the dark
RS07G
months
3
Properties of cured unreinforced resin Distitron 110BX
Properties
Test method
Unit
Typical value
Tensile strength
ISO 527-1993
MPa
65
Tensile modulus
ISO 527-1993
MPa
3400
Elongation at break
ISO 527-1993
%
2.6
Flexural strength
ISO 178-2001
MPa
125
Flexural modulus
ISO 178-2001
MPa
3200
Heat deflection temperature
ISO 75 - 2:2004 Method A
°C
92
Glass transition
ASTM E 1545-00
°C
108
Barcol hardness at 25°C
ASTM D 2583-01
Unit
39
Full data sheet
Contact
Close
DISTITRON 110 SV2Z
Delivery specification of the liquid resin Distitron 110SV2Z
Properties
Test method
Unit
Value
Viscosity RVF at 25°C, s 3 rpm 20
ISO 2555
mPa.s
190 - 260
Monomer content
RS06C
%
33 - 37
Curing at 20°C with
0.35% Co6% + 1.5% MEKP
Gel time
RS08G
min.sec
29.00 - 34.00
Curing time
RS08G
min.sec
35.00 - 45.00
Maximum temperature
RS08G
°C
170 - 200
Properties of the liquid resin Distitron 110SV2Z
Properties
Test method
Unit
Value
Appearance - colour
RS13F
-----
Opalescent orange rose
Acid number
RS02C
mg KOH/g
16 - 23
Stability at 20°C in the dark
RS07G
months
3
Properties of cured unreinforced resin Distitron 110SV2Z
Properties
Test method
Unit
Typical value
Tensile strength
ISO 527-1993
MPa
75
Tensile modulus
ISO 527-1993
MPa
3300
Elongation at break
ISO 527-1993
%
4,5
Yield strength
ISO 527-1993
MPa
75
Creep
ISO 527-1993
%
4,2
Flexural strength
ISO 178-2001
MPa
120
Flexural modulus
ISO 178-2001
MPa
3400
Heat deflection temperature
ISO 75/A
°C
78
Barcol hardness at 25°C
ASTM D 2583-01
Unit
40
Full data sheet
Contact
Close
DISTITRON 120 ABV2,5
Delivery specification of the liquid resin Distitron 120ABV2.5
Properties
Test method
Unit
Typical value
Viscosity RVF at 25°C, s 2 rpm 20
GM025
mPa.s
180 - 260
Monomer content
RS06C
%
36 - 41
Curing at 25°C with
0,48% Co 1% + 1,5% MEKP
Gel time
RS08G
min.sec
4.00 - 8.00
Curing time
RS08G
min.sec
7.00 - 15.00
Maximum temperature
RS08G
°C
205 - 230
Properties of the liquid resin Distitron 120ABV2.5
Propiedades
Método de la prueba
Unidad de medida
Valor
Appearance - colour
RS13F
-----
Yellow
Acid number
RS02C
mg KOH/g
11 - 19
Stability at 20°C in the dark
RS07G
months
3
Properties of cured unreinforced resinDistitron 120ABV2.5
Properties
Test method
Unit
Typical value
Tensile strength
ISO 527-1993
MPa
65
Tensile modulus
ISO 527-1993
MPa
3200
Elongation at break
ISO 527-1993
%
2,5
Flexural strength
ISO 178-2001
MPa
113
Flexural modulus
ISO 178-2001
MPa
3100
Glass transition
ASTM E 1545-00
°C
111
Heat deflection temperature
ISO 75/A - 2:2004 Método A
°C
109
Barcol hardness at 25°C
ASTM D 2583-01
Unit
44
Full data sheet
Contact
Close
DISTITRON I 100 SV1,5
Delivery specification of the liquid resin Distitron I100SV1,5
Properties
Test method
Unit
Typical value
Viscosity RVF at 25°C, s 2 rpm 20
GM025
mPa.s
120 - 160
Monomer content
RS06C
%
35 - 40
Curing at 20°C with
1,5% MEKP
Gel time
RS08G
min.sec
58.00 - 68.00
Curing time
RS08G
min.sec
76.00 - 96.00
Maximum temperature
RS08G
°C
135 - 165
Properties of the liquid resin Distitron I100SV1,5
Properties
Test method
Unit
Typical value
Appearance - colour
RS13F
-----
Orange rose
Stability at 20°C in the dark
RS07G
months
3
Properties of cured unreinforced resin Distitron I100SV1,5
Properties
Test method
Unit
Typical value
Tensile strength
ISO 527-1993
MPa
75
Tensile modulus
ISO 527-1993
MPa
3500
Elongation at break
ISO 527-1993
%
3,8
Flexural strength
ISO 178-2001
MPa
130
Flexural modulus
ISO 178-2001
MPa
3500
Heat deflection temperature
ISO 75 - 2:2004
Method A
°C
79
Barcol hardness at 25°C
ASTM D 2583-01
Unit
42
Full data sheet
Contact
Close
6818 TAQ8
Características métodos y condiciones
Valores (Valores promedio)
Físicas
Peso especifico a 20 °C :
1.10 g/cm³
Viscosidad (dPa.s ) : V25
Brookfield a 23 °C
M2V50 :
4-5
Extracto seco (%) : PC53
58-62
Reactividad :
Método :
R 151 (Ensayo en tubo)
Temperatura de ensayo :
23 °C
Sistema catalitico :
1.5 % PMEK 50
Tiempo de gel :
20 – 24 min
Tiempo total :
35 – 45 min
Temperatura de pic :
110 – 130 °C
Propiedades mecánicas (resina polimerizada no reforzada)
Postcurado (16 h a 40°C + 2 h a 90°C)
Tracción ISO 527 (1999):
-Módulo de tracción (MPa) :
3813
-Resistencia a tracción (MPa) :
58
-Elongación a rotura (%) :
2.2
Flexión ISO 178 (2003):
-Resistencia a flexión (MPa) :
94
-Módulo de flexión (MPa) :
3520
Propiedades termomecánicas (resina polimerizada no
reforzada)
-HDT ISO 75-2 A (1999) (°C) :
67 (2 h a 120°C)
Propiedades mecánicas en laminado
(4 mats 450 g/m²) - Postcurado 16 h a 40°C
Tracción ISO 527 (1999):
-Resistencia a tracción (MPa) :
110
-Elongación a rotura (%) :
1.9
Flexión ISO 178 (2003):
-Resistencia a flexión (MPa) :
200
-Módulo de flexión (MPa) :
7600
Full data sheet
Contact
Close
Close
Food
152F
Delivery specification of the liquid resin Distitron 152F
Properties
Test method
Unit
Value
Viscosity RVF at 25°C, s 3 rpm 20
GM025
mPa.s
850 - 1150
Monomer content
RS06C
%
32 - 36
Curing at 25°C with
0.2% Co6% + 2% MEKP 5.00
Gel time
RS08G
min.sec
5.00 - 8.00
Curing time
RS08G
min.sec
11.00 - 18.00
Maximum temperature
RS08G
°C
180 - 210
Properties of the liquid resin Distitron 152F
Properties
Test method
Unit
Value
Appearance - colour
RS13F
-----
Light yellow
Acid number
RS02C
mg KOH/g
16 - 23
Stability at 20°C in the dark
RS07G
months
6
Properties of cured unreinforced resin Distitron 152F
Properties
Test method
Unit
Value
Tensile strength
ISO 527-1993
MPa
80
Tensile modulus
ISO 527-1993
MPa
3700
Elongation at break
ISO 527-1993
%
3.3
Flexural strength
ISO 178-2001
MPa
125
Flexural modulus
ISO 178-2001
MPa
3800
Heat deflection temperature
ASTM E 1545-00
°C
84
Glass transition
ISO 75 - 2:2004 Method A
°C
95
Barcol hardness at 25°C
ASTM D 2583-01
Unit
45
Full data sheet
Contact
Close
183F
Copia de Especificaciones de la resina Distriton 183F líquida
Propiedades
Método de la prueba
Unidad de medida
Valor
Peso específico a 20°C
g/cm³
1,14
Viscosidad Brookfield a 25°C, eje 3 rpm 20
MT-CU025V
mPa.s
900 - 1100
Extracto seco
MT-CU001C
%
63 - 67
Reactividad
a 25°C + 0,3% Co 6% + 1%
MEKP50
Tiempo de gel
RS08G
min.sec
12 - 16
Delta
RS08G
min.sec
6 - 11
Temperatura de pico
RS08G
°C
185 - 215
Acidez
MT-CU001I
mgKOH/g
13 - 20
Estabilidad a 23°C en oscuridad
MT-CU002S
meses
4
Copia de Propiedades generales de la resina Distitron 183F líquida
Propiedades
Método de la prueba
Unidad de medida
Valor
Postcurado
24h a 23°C + 2h a 100°C + 1h a 100 ° C
Resistencia a tracción
ISO 527 (2012)
MPa
80
Módulo de tracción
ISO 527 (2012)
MPa
3500
Elongación a rotura
ISO 527 (2012)
%
4,3
Resistencia a flexión
ISO 178/B (2010)
MPa
140
Módulo de flexión
ISO 178/B (2010)
MPa
3400
HDT - Temperatura de flexión bajo carga
ISO 75 -2A (2013)
°C
94
Temperatura de transición vítrea
ASTM E 1545 (2011)
°C
103
Dureza Barcol a 25°C
ASTM D 2583 (2007)
Unidades
41
Full data sheet
Contact
Close
1402F
Delivery specification of the liquid resin Distitron 1402F
Properties
Test method
Unit
Value
Viscosity RVF at 25°C, s 3 rpm 20
GM025
mPa.s
630 - 780
Monomer content
RS06C
%
31 - 35
Curing at 25°C with
0,9% Co1% + 2% MEKP
Gel time
RS08G
min.sec
9.00 - 15.00
Curing time
RS08G
min.sec
15.00 - 27.00
Maximum temperature
RS08G
°C
170 - 200
Properties of the liquid resin Distitron 1402F
Properties
Test method
Unit
Value
Appearance - colour
RS13F
-----
Light yellow
Acid number
RS02C
mg KOH/g
24 - 31
Stability at 20°C in the dark
RS07G
months
6
Properties of cured unreinforced resin Distitron 1402F
Properties
Test method
Unit
Value
Tensile strength
ISO 527-1993
MPa
80
Tensile modulus
ISO 527-1993
MPa
4100
Elongation at break
ISO 527-1993
%
2,8
Flexural strength
ISO 178-2001
MPa
140
Flexural modulus
ISO 178-2001
MPa
4200
Heat deflection temperature
ISO 75 - 2:2004 Method A
°C
73
Barcol hardness at 25°C
ASTM D 2583-01
Unit
45
Full data sheet
Contact
Close
1629F
Delivery specification of the liquid resin Distitron 1629F
Properties
Test method
Unit
Value
Viscosity RVF at 25°C, s 2 rpm 20
GM025
mPa.s
270 - 330
Monomer content
RS06C
%
38 - 43
Curing at 25°C with
0.3% Co6% + 1% MEKP
Gel time
RS08G
min.sec
7.00 - 11.00
Curing time
RS08G
min.sec
14.00 - 22.00
Maximum temperature
RS08G
°C
185 - 215
Properties of the liquid resin Distitron 1629F
Properties
Test method
Unit
Value
Appearance - colour
RS13F
-----
Light yellow
Acid number
RS02C
mg KOH/g
11 - 18
Stability at 20°C in the dark
RS07G
months
3
Properties of cured unreinforced resin Distitron 1629F
Properties
Test method
Unit
Typical value
Tensile strength
ISO 527-2012
MPa
75
Tensile modulus
ISO 527-2012
MPa
3800
Elongation at break
ISO 527-2012
%
2.6
Flexural strength
ISO 178-2010 Method B
MPa
135
Flexural modulus
ISO 178-2010 Method B
MPa
3700
Heat deflection temperature
ISO 75 - 2:2004 Method A
°C
105
Glass transition
ASTM E 1545-11
°C
112
Barcol hardness at 25°C
ASTM D 2583-07
Unit
45
Full data sheet
Contact
Close
Close
Vinylester
DISTITRON VE 100
Delivery specification of the liquid resin Distitron VE100
Properties
Test method
Unit
Value
Viscosity RVF at 25°C, s 2 rpm 2
GM025
mPa.s
380 - 480
Monomer content
RS06C
%
42 - 46
Curing at 25°C with
0.5% Co6% + 1.5% Cumyl hydroperoxyde
Gel time
RS08G
min.sec
11.00 - 15.00
Curing time
RS08G
min.sec
19.00 - 28.00
Maximum temperature
RS08G
°C
165 - 195
Properties of the liquid resin Distitron VE100
Properties
Test method
Unit
Value
Appearance - colour
RS13F
-----
Yellow
Acid number
RS02C
mg KOH/g
8 max
Stability at 20°C in the dark
RS07G
months
6
Properties of cured unreinforced resin Distitron VE100
Properties
Test method
Unit
Typical value
Tensile strength
ISO 527-2012
MPa
85
Tensile modulus 3200
ISO 527-2012
MPa
3200
Stress at yield
ISO 527-2012
MPa
85
Strain at yield
ISO 527-2012
%
5.0
Nominal strain at break
ISO 527-2012
%
6,6
Flexural strength
ISO 178-2010 Method B
MPa
145
Flexural modulus
ISO 178-2010 Method B
MPa
3300
Glass transition
ASTM E 1545-11
°C
114
Heat deflection temperature
ISO 75 - 2:2004 Method A
°C
106
Overall volume shrinkage
ISO 3521-1997 corr. 1:2003
%
7.3
Barcol hardness at 25°C
ASTM D 2583-07
Unit
37
Full data sheet
Contact
Close
DISTITRON VE 100 ST
Delivery specification of the liquid resin Distitron VE100ST
Properties
Test method
Unit
Value
Viscosity RVF at 25°C, s 2 rpm 2
GM025
mPa.s
1900 - 2600
Viscosity RVF at 25°C, s 2 rpm 20
GM025
mPa.s
610 - 840
Monomer content
RS06C
%
44 - 49
Curing at 25°C with
1,5% MEKP
Gel time
RS08G
min.sec
21.00 - 30.00
Curing time
RS08G
min.sec
38.00 - 56.00
Maximum temperature
RS08G
°C
150 - 180
Properties of the liquid resin Distitron VE100ST
Properties
Test method
Unit
Value
Appearance - colour
RS13F
-----
Opalescent violet
Stability at 20°C in the dark
RS07G
months
3
Properties of cured unreinforced resin Distitron VE100ST
Properties
Test method
Unit
Typical value
Tensile strength
ISO 527-1993
MPa
55
Tensile modulus
ISO 527-1993
MPa
3400
Elongation at break
ISO 527-1993
%
2,0
Flexural strength
ISO 178-2001
MPa
90
Flexural modulus
ISO 178-2001
MPa
3500
Glass transition
ASTM E 1545-00
°C
106
Heat deflection temperature
ISO 75 - 2:2004 Method A
°C
100
Overall volume shrinkage
ISO 3521-1997 corr. 1:2003
%
8.0
Barcol hardness at 25°C
ASTM D 2583-01
Unit
35
Full data sheet
Contact
Close
DISTITRON VE 100 STD
Delivery specification of the liquid resin Distitron VE100STD
Properties
Test method
Unit
Typical value
Viscosity RVF at 25°C, s 2 rpm 2
GM025
mPa.s
1900 - 2600
Viscosity RVF at 25°C, s 2 rpm 20
GM025
mPa.s
600 - 850
Monomer content
RS06C
%
44 - 49
Curing at 25°C with
1,5% MEKP
Gel time
RS08G
min.sec
34.00 - 41.00
Curing time
RS08G
min.sec
55.00 - 72.00
Maximum temperature
RS08G
°C
145 - 175
Properties of the liquid resin VE100STD
Properties
Test method
Unit
Typical value
Appearance - colour
RS13F
-----
Opalescent violet
Stability at 20°C in the dark
RS07G
months
3
Properties of cured unreinforced resin Distitron VE100STD
Properties
Test method
Unit
Typical value
Tensile strength
ISO 527-1993
MPa
55
Tensile modulus
ISO 527-1993
MPa
3400
Elongation at break
ISO 527-1993
%
2,0
Flexural strength
ISO 178-2001
MPa
95
Flexural modulus
ISO 178-2001
MPa
3500
Heat deflection temperature
ISO 75 - 2:2004 Method A
°C
105
Glass transition
ASTM E 1545-00
°C
110
Barcol hardness at 25°C
ASTM D 2583-01
Unit
35
Full data sheet
Contact
Close
DISTITRON VE 370 SCD
Delivery specification of the liquid resin Distitron VE370SCD
Properties
Test method
Unit
Typical value
Viscosity RVF a 25 °C , s 2 rpm 20
GM025
mPa.s
120 - 140
Monomer content
RS06C
%
44 - 49
Curing at 25°C with
0,3% Co6% + 1,5% Cumyl hydroperoxide
Gel time
RS08G
min.sec
95,00 - 115,00
Curing time
RS08G
min.sec
135,00 - 175,00
Maximum temperature
RS08G
°C
120 - 150
Properties of the liquid resin Distitron VE370SCD
Properties
Test method
Unit
Typical value
Appearance - colour
RS13F
-----
Yellow-brown
Acid number
RS02C
mg KOH/g
<10
Stability at 20°C in the dark
RS07G
months
4
Properties of cured unreinforced resin Distitron VE370SCD
Properties
Test method
Unit
Typical value
Resistencia a la tracción
ISO 527-1993
MPa
85
Tensile strength
ISO 527-1993
MPa
3500
Elongation at break
ISO 527-1993
%
6,6
Stress at yield
ISO 527-1993
MPa
85
Strain at yield
ISO 527-1993
%
5,0
Flexural strength
ISO 178-2001
MPa
145
Flexural modulus
ISO 178-2001
MPa
3600
Heat deflection temperature
ISO 75 - 2:2004 Method A
°C
108
Glass transition
ASTM E 1545-00
°C
115
Barcol hardness at 25°C
ASTM D 2583-01
Unit
40
Full data sheet
Contact
Close
Close
Close
Gelcoats
Industrial
Isoftalic
ISO-NPG
Mold
Topcoat
Close
Putties
With fiber
No fiber
Low density
Vinylester
Close
Fiberglasses
MAT (CSM) Emulsion
CSM 100
CSM 125
CSM 150
CSM 225
CSM 300
CSM 450
CSM 600
CSM 900
Close
MAT (CSM) Powder
CSM 300
CSM 450
CSM 600
Close
Direct Roving
BEŞLER DR 1200 TEX
BEŞLER DR 2400 TEX
BEŞLER DR 4800 TEX
Close
Projection and Cut Roving
BEŞLER SPRAY-UP R 2400 TEX
Close
Roving Fabrics
EWR 300
EWR 500
EWR 800
Close
Unidirectional Fabric
UD 500
UD 600
UD 800
UD 1200
Close
Bidirectional Fabric
TDS 600/300
TDS 600/450
TDS 800/300
TDS 800/450
TDS 1700/300
Close
Complex Fabrics (Fabric/MAT)
TDS 300/300
TDS 500/450
TDS 600/300
TDS 800/300
TDS 800/450
Close
Fibercore
200/180/200
300/180/300
450/180/450
600/180/600
Close
Veils and Meshes
ECR 30gr – 50m
ECR 30gr – 250m
Vr72
Close
Close
Equipment
80 ml dispenser
Close
Cutting machine
Close
Hard bristle rollers
Close
Special rollers
Close
Impregnation rollers
Close
Metal rollers
Close
Nylon rollers
Close
Close
Cores
Viledon
TSD PRODUCT MATRIX CORE MATERIAL
Product
Thickness (mm)
Weight (g/m2)
Roll length
Roll width (mm)
T1722HC
2.2
55
110
1000
T1723HC
3.2
75
80
1000
T1724HC
4.4
100
60
1000
T1725HC
5.2
120
50
1000
Full data sheet
Contact
Close
PVC foam
Physical and chemical properties
Appearence
Sheet or tape
Colour
White
Odour
Odourless
Boling point/Boiling range
ºC
Not applicable
Melting point
ºC
250-260ºC (PET)
Freezing temperature
ºC
Not applicable
Flash point
ºC
350-400ºC (PET)
Ignition temperature
ºC
420ºC (PET)
Auto ignition
Not applicable
Explosion hazard
Not applicable
Explosion limits
Vol.-%
Not applicable
Vapour pressure
mbar
Not applicable
Density
g/cm3
22 g/m2
Bulk density
kg/m3
Not applicable
Solubility in water
Insoluble
Solubility in other solvents
Insoluble in most solvents
pH-value
Not applicable
Viscosity
Not applicable
Additional information
None
Full data sheet
Contact
Close
PVC foams (Divinicell H)
Mechanical properties Divinycell H
Property
Test Procedure
Unit
H35
H45
H60
H80
H100
H130
H160
H200
H250
Compressive Strength
ASTM D 1621
MPa
Nominal
0.5
0.6
0.9
1.4
2.0
3.0
3.4
5.4
7.2
Mínimo
0.3
0.5
0.7
1.15
1.65
2.4
2.8
4.5
6.1
Compressive Modulus
ASTM D1621-B-73
MPa
Nominal
40
50
70
90
135
170
200
310
400
Mínimo
29
45
60
80
115
145
175
265
350
Tensile Strength
ASTM D 1623
MPa
Nominal
1.0
1.4
1.8
2.5
3.5
4.8
5.4
7.1
9.2
Mínimo
0.8
1.1
1.5
2.2
2.5
3.5
4.0
6.3
8.0
Tensile Modulus
ASTM D 1623
MPa
Nominal
49
55
75
95
130
175
205
250
320
Mínimo
37
45
57
85
105
135
160
210
260
Shear Strength
ASTM C 273
MPa
Nominal
0.4
0.56
0.76
1.15
1.6
2.2
2.6
3.5
4.5
Mínimo
0.3
0.46
0.63
0.95
1.4
1.9
2.2
3.2
3.9
Shear Modulus
ASTM C 273
MPa
Nominal
12
15
20
27
35
50
60
73
97
Mínimo
9
12
16
23
28
40
50
65
81
Shear Strain
ASTM C 273
%
Nominal
9
12
20
30
40
40
40
45
45
Density
ISO 845
kg/m3
Nominal
38
48
60
80
100
130
160
200
250
Physical characteristics Divinycell H
Characteristics
Unit
H35
H45
H60
H80
H100
H130
H160
H200
H250
Tipo de test
Density variation
%
-10%/+20%
± 10
± 10
± 10
± 10
± 10
± 10
± 10
± 10
-
Thermal conductivity
W/(m-K)
0.028
0.028
0.029
0.031
0.033
0.036
0.040
0.044
0.049
EN 12667
Coeff, linear heat expansion
x10-6/°C
40
40
40
40
40
40
40
40
40
ISO 4897
Heat Distortion Temperature
°C
+125
+125
+125
+125
+125
+125
+125
+125
+125
DIN 53424
Continous temp range
°C
-200/+70
-200/+70
-200/+70
-200/+70
-200/+70
-200/+70
-200/+70
-200/+70
-200/+70
-
Max process temp
°C
+90
+90
+90
+90
+110
+110
+110
+110
+110
-
Dissipation factor
-
0.0001
0.0002
0.0003
0.0005
0.0006
0.0009
0.0012
0.0015
0.0019
ASTM D 2520
Dielectric constant
-
1.04
1.05
1.06
1.09
1.11
1.15
1.18
1.23
1.29
ASTM D 2520
Poissons ratio
-
0.4
0.4
0.4
0.4
0.4
0.4
0.4
0.4
0.4
D638-08
Physical characteristics Divinycell H
Format
Unit
H35
H45
H60
H80
H100
H130
H160
H200
H250
Plain sheets
Length
mm
2650
2440
2440
2440
2160
1960
1860
1730
1640
Width
mm
1250
1220
1220
1220
1070
970
915
850
800
GS sheet
Length
mm
1250
1220
1220
1220
1080
980
930
865
-
Width
mm
883
813
813
813
1070
970
915
850
-
GS sheet
Length
mm
1250
1220
1220
1220
-
-
-
-
-
Width
mm
1250
1220
1220
1220
-
-
-
-
-
Full data sheet
Contact
Close
PET foams (Divinicell P)
Mechanical properties Divinycell P
Property
Test Procedure
Unit
P60
P100
P150
Compressive Strength
ASTM D 1621
psi
Nominal
102
218
334
Minimum
65
160
290
Compressive Modulus
ASTM D1621-B-73
psi
Nominal
9,427
14,504
22,046
Minimum
4,206
8,702
16,679
Tensile Strength
ASTM D 1623
psi
Nominal
174
261
355
Minimum
116
196
268
Shear Strength
ISO 1922
psi
Nominal
65
123
181
Minimum
46
100
138
Shear Modulus
ISO 1922
psi
Nominal
1,885
4,061
5,802
Minimum
1,378
3,191
5,221
Shear Elongation
ISO 1922
%
Nominal
20
12
7,5
Minimum
8
3
3
Density
ISO 845
kg/m3
Nominal
4,1
6,9
9,4
Technical Characteristics Divinycell P
Characteristics
Unit
P60
P100
P150
Test method
Density
%
± 7
± 6
± 5
-
Thermal conductivity
Btu x in / ft2 x h x ºF)
0.229
0.229
TBD
ISO 4897
Fire resistance class
-
S4 ST2 SR2
S4 ST2 SR2
S4 ST2 SR2
DIN 5510
-
M1 F1
M1 F1
M1 F1
AFNOR NF F 16-101
Physical characteristics Divinycell P
Format
Unit
P60
P100
P160
Plain sheets
Length
inch
96.06
96.06
96.06
Width
inch
48.03
48.03
48.03
GS sheet
Length
inch
48.03
48.03
48.03
Width
inch
48.03
48.03
48.03
Full data sheet
Contact
Close
Close
Mould release agents
Mould release waxes
333MR
333MR-112407
Weight:
412 Grams per can
Flash Point:
122 ºF/ 50 ºC
Shelf Life:
1 year from date of shipment
Color:
Blue
V.O.C.:
483.50 Grams per liter
Full data sheet
Contact
Close
1000P
1000P-112407
Weight:
412 Grams per can
Flash Point:
98 ºF / 36.66 ºC
Shelf Life:
1 year from date of shipment
Color:
Color:
Yellow Paste Wax
V.O.C.:
477.50 Grams per liter
Full data sheet
Contact
Close
FK 888
FK 888
Weight:
312 Grams per can
Flash Point:
100ºF (38ºC)
Shelf Life:
1 year from date of shipment
Color:
Gold
V.O.C.:
3.98 lbs/gal (477.50 g/l)
Full data sheet
Contact
Close
Close
Semi-permanent mould release agent
135T
135T-TData-052113
Weight:
7.27 Lbs per gallon
Flash Point:
50ºF/ 10 ºC
Shelf life:
1 year from date of shipment
V.O.C.:
724.14 grams per liter
Full data sheet
Contact
Close
Close
Mould cleaner and sealer
69
69-113007
Weight:
7 lbs per gallon
Flash Point:
112º F
Shelf life:
1 year from date of shipment
V.O.C.:
7 lbs per gallon
Full data sheet
Contact
Close
86
86-112207
Weight:
6.92 pounds per gallon
Flash Point:
109º F TCC
Shelf Life:
1 year from date of shipment
V.O.C.:
6.31 Lbs/gal (756.19 g/l)
Full data sheet
Contact
Close
Close
Close
Ecological cleaner
Dilynt
Product specification Di-LYNT ES
Characteristics
Unit
Value
Method
Reference
Appearance
Clear liquid
L000
Moisture
%
0.5 max
GM 010
ASTM E-203
Typical properties Di-LYNT ES
Characteristics
Unit
Value
Colour
Colorless - light yellow
Odour
typical
Density @ 25°C
g/ml
1.04
Viscosity @ 25°C
mPa.s
2.01
Melting point/range
ºC
-20
Boiling point/range
ºC
215
Vapour pressure @ 20°C
Pa
<10
Flash point cc (ASTM D93-07)
ºC
90
Log POW (OECD 117-2004)
1.4
Full data sheet
Contact
Close
Close
Catalysts and accelerators
MEKP Methyl Ethyl Ketone Peroxide
P200F
General information P200F
Characteristic
Unit
Value
Appearance
-
Liquid
Colour - Odour
-
Colourless - Characteristic
Active oxygen content
%
9,1
Peroxides
%
>35%
Flegmatizer – Dimethyl phthalate/DiacetoneAlcohol
%
>40%
Boiling point/ interval
°C
100°C decompose !
Flash point (open cup – C.O.C.)
°C
90°C
Flammability ASTM D-4206-96(2001)
-
Not support the combustion
Explosive properties
-
Product is not explosive
SADT (Self Accelerated Decomposition Temperature)
°C
>60
Relative density UNI EN ISO 12185-00
d 20/20
1,200 (PRO 2011)
Viscosity at 20 °C ISO UNI EN 3104
mPa.s
23 - 26 (PRO 2011)
Full data sheet
Contact
Close
P200TX
Physical and chemical properties P200TX
Characteristic
Unit of measure
Declared value
SADT
°C
> 65°C
Active oxygen content
%
9,8 – 9,9
Peroxide content
%
32 - 37%
Appearence, Colour
-
Liquid, clear, Colorless
Odour
-
Distinctive - Aceton like
pH (in aqueous solution)
-
Slightky acid - < 5
Boiling point/interval
°C
>60ºC - Decomposes
Melting point/interval
°C
< - 25
Flash Point Closed-Cup ASTM D3278
°C
> 75 °C at 1013 hPa
Oxidizing properties
-
Organic peroxide
Vapour pressure
Pa
73,6 Pa at 25°C
Relative density UNI EN ISO 12185-00
d 20/20
1,011 - 1,015 (SSC 2010 Promox P211TX)
Solubility in water
-
6,530 mg/l at 20 °C
Solubility in Organic Solvents
-
Soluble in most organic solvents
Partition coefficient OECD 117
LogKow/LogPow
log Kow : < 0,3 (OCDE 117)
Explosive properties
The substance or mixture is an organic peroxide classified as type D
Full data sheet
Contact
Close
P211TX
Physical and chemical properties P211TX
Characteristic
Unit of measure
Declared value
SADT
°C
> 65°C
Active oxygen content
%
9,8 – 9,9
Peroxide content
%
32 - 37%
Appearence, Colour
-
Liquid, clear, Colorless
Odour
-
Distinctive - Aceton like
pH (in aqueous solution)
-
Slightky acid - < 5
Boiling point/interval
°C
No aplicable – > 100 °C Se descompone al calentar.
Melting point/interval
°C
< - 25
Flash Point Closed-Cup ASTM D3278
°C
> 75 °C at 1013 hPa
Oxidizing properties
-
Organic peroxide
Vapour pressure
Pa
73,6 Pa at 25°C
Relative density UNI EN ISO 12185-00
d 20/20
1,011 - 1,015 (SSC 2010 Promox P211TX)
Solubility in water
-
6,530 mg/l at 20 °C
Solubility in Organic Solvents
-
Soluble in most organic solvents
Partition coefficient OECD 117
LogKow/LogPow
log Kow : < 0,3 (OCDE 117)
Explosive properties
La sustancia o mezcla es un peróxido orgánico clasificado como tipo D.
Full data sheet
Contact
Close
P250
Physical and chemical properties P250
Characteristic
Unit of measure
Declared value
Aspecto
-
Líquido, claro
Color
-
Incoloro
Contenuto in ossigeno attivo
%
8,2
Contenuto in perossidi
%
37
Contenuto in diiso butil ftalato / diaceton alcol
%
>55
Punto/intervallo di ebollizione
ºC
100°C decompone !
Punto di infiammabilità (vaso chiuso)
ºC
80
Infiammabilità ASTM D-4206-96 (2001)
-
non sostiene la combustione
SADT (Self Accelerated Decomposition Temperature)
ºC
>60ºC
Densità relativa UNI EN ISO 12185-00
d 20/20
1.060
Viscosità a 20 °C ISO UNI EN 3104
mPa.s
30
Full data sheet
Contact
Close
Close
AAP. Acetylacetone Peroxide
P300
General information P300
Characteristic
Unit of measure
Declared value
Appearance - at 20°C e 1013 hPa
-
Liquid, clear
Colour
-
Colourless
Odour
-
Distinctive – Aceton Like
Substance
-
Organic
pH (in aqueous solution) - EPA OPPTS 830.7000
-
Slightly Acid - pH ca. 4,0
Melting point/freezing point – EPIWIN (v. 4.00)
°C
< -10 °C at 1013 hPa
Melting point/freezing point – Promox
°C
< -15 °C at 1013 hPa
Boiling point/range
°C
>100°C – Decomposes
Relative density DIN ISO 3507109
g/cm3
1,0514 g/cm3 at 20 °C
Relative density UNI EN ISO 12185:1999 a 20°C
d 20/20
1,037 – 1,044 (SSC2010 – Promox P300)
Vapour Pressure – ASTM E1782-08
PENTANE-2,4-DIONE PEROXYDE
20 hPa at 20°C
4-HYDROXY-4-METHYLPENTANE-2-ONE
1.29 hPa at 20°C
HYDROGEN PEROXIDE
10,1 m Hg @ 20ºC (HP50%)
Vapour Density
> 1 Referred to Air =1
Partition coefficient OECD 117 LogKow/LogPow
PENTANE-2,4-DIONE PEROXYDE
log Kow : 1,1, Slightly bioaccumulable.
4-HYDROXY-4-METHYLPENTANE-2-ONE
log Kow : - 0,09
PENTANE-2,4-DIONE
log Kow : 0,68 , at 40 °C
HYDROGEN PEROXIDE
log Kow : - 1,57
Solubility in water – EU method A.6
PENTANE-2,4-DIONE PEROXYDE
> 500 g/l at 20 °C
PENTANE-2,4-DIONE PEROXYDE
> 500 g/l at 20 °C
PENTANE-2,4-DIONE
16 g/100 ml
Solubility in Organic Solvents – CIPAC MT 181
g/l
Soluble in most organic solvents
ETHYL ACETATE
> 500 g/l
METHANOL
> 500 g/l
HEXANE
< 50 g/l
Surface tension EU Method A.5.
mN/m
Not determined
Flash Point - Cleveland open cup ASTM D92
°C
> 85°C at 1013 hPa
Flash Point - Penski-Martens closed cup EN ISO 2719
°C
> 70°C at 1013 hPa
AutoFlammability EU Method A.15
°C
Non Applicable
Flammability – in Contact with Water
°C
Negative
Flammability – Pirofosforic Properties
°C
Not determined
Self-ignition temperature
°C
> 180°C
Explosive properties – EU Method A.14
The substance or mixture is an organic peroxide classified as type D.
Oxidizing properties/Comburent
Not applicable
Organic peroxide
Dissociation Costant – SPARC pKa 20°C
-HYDROXY-4-METHYLPENTANE-2-ONE
14.57 a 20°C
HYDROGEN PEROXIDE
11,62 - pKa
Viscosity at 20 °C OECD GuideLine 114
mPa∙s
23 (Dinamica)
Viscosity at 20 °C UNI EN ISO 3104:2000 a 20°C
mm2/s
22 - 24 (SSC 2010 – Promox P300)
Henry’s Law Costant at 25°C. Pa m3/mole
HYDROGEN PEROXIDE
750E-06 Pa.m3/mol, at 20 °C – 70%
Stability into Organic Solvents
Stable in his formulation agents
VOC Content (VOC)
% w/w
NA
SADT (Self Accelerated Decomposition Temperature)
°C
> 60°C
Active oxygen content
%
4,2 – 4,4
Peroxide content
%
30 – 33%
Miscibility with Solvents
-
See chapter 10
Full data sheet
Contact
Close
Close
Cumene Hydroperoxyde
P600
General information P600
Characteristic
Unit of measure
Declared value
Appearance
-
Liquid, clear
Colour
-
Colourless
Odour
-
Distinctive
pH (in aqueous solution)
-
Acid
Boiling point/ interval
°C
100°C decomposes
Flash point (open cup)
°C
60
Flash point (closed cup) - EN ISO 3680
°C
Not determined
Flammability ASTM D-4206-96(2001)
-
Not sustain combustion
Explosive properties
-
Product is not explosive.
Oxidizing properties
-
Not applicable
Vapour pressure
-
Not determined
Relative density UNI EN ISO 12185:1999 at 20°C
d 20/20
1,020
Solubility in water
-
Partly soluble
Liposolubility
-
Soluble in polar solvents
Partition coefficient
logPow
Not determined
Viscosity at 20 °C UNI EN ISO 3104:2000 at 20°C
mm2/s
05
Steam density
aria=1
Not determined
Refractive Index
-
Not determined
VOC Content
%
Not determined
Auto ignition
°C
Not determined
Melting point/ interval
°C
< - 10
SADT (Self Accelerated Decomposition Temperature)
°C
> + 60
Active oxygen content
%
4,6
Solubility in other solvents
-
See section 10
Full data sheet
Contact
Close
Close
Cobalt Octoate
Cobalt 6%
Copia de Propiedades físicas y químicas Cobalt 6%
Characteristic
Declared value
Physischer Zustand bei 20 ºC:
Flüssigkeit
Aussehen:
Nicht verfügbar
Farbe:
Kobaltblau
Geruch:
Nicht verfügbar
Siedetemperatur bei atmosphärischem Druck:
206 ºC
Dampfdruck bei 25 ºC:
71 Pa
Dampfdruck bei 50 ºC:
363 Pa (0 kPa)
Verdunstungsrate bei 25 ºC:
Nicht relevant *
Dichte bei 25 ºC:
850 - 950 kg/m³
Relative Dichte bei 25 ºC:
0,9
Dynamische Viskosität bei 25 ºC:
60 cP
Viskositäts-Dichteverhältnis bei 25 ºC:
66 cSt
Viskositäts-Dichteverhältnis bei 40 ºC:
No relevante
Konzentration:
No relevante
pH:
No relevante
Dampfdichte bei 25 ºC:
No relevante
Verteilungskoeffizient n-Octanol/Wasserr bei 25 ºC:
No relevante
Wasserlöslichkeit bei 25 ºC:
No relevante
Löslichkeitseigenschaft:
No relevante
Zersetzungstemperatur:
No relevante
Schmelzpunkt/Gefrierpunkt:
No relevante
Entflammungstemperatur:
61 ºC
Selbstentflammungstemperatur:
265 ºC
Untere Entflammbarkeitsgrenze:
No relevante
Obere Entflammbarkeitsgrenze:
No relevante
Oberflächenspannung bei 25 ºC:
No relevante
Brechungsindex:
No relevante
Full data sheet
Contact
Close
Close
Close
Polyurethanes
Baymer Spray 145
BAYMER SPRAY 145 Properties
Property
Value
Unit
Method
Hydroxyl number 197
210 ± 20
mg KOH/g
LPUR - 048
Water content
2,8 ± 0,14
%
LPUR - 001
Viscosity 25ºC 350 ±
350 ± 200
mPa·s
LPUR - 002
Density 23ºC
aprox. 1,20
g/cm³
LPUR-050
Full data sheet
Contact
Close
Byamer Spray 150
BAYMER SPRAY 150 Properties
Property
Value
Unit of
measurement
Method
Hydroxyl number
230 ± 30
mg KOH/g
LPUR - 048
Water content
2,8 ± 0,14
%
LPUR - 001
Viscosity a 25ºC 350 ±
350 ± 200
mPa·s
LPUR - 002
Density 23ºC
aprox. 1,20
g/cm³
LPUR-050
Full data sheet
Contact
Close
Desmodur 44V20
DESMODUR 44V20L Properties
Property
Value
Unit of
measurement
Method
NCO content
30.5 - 32.5
% by wt.
MDI-01-01
Viscosity 25 °C*)
160 - 240
mPa·s
MDI-01-02
Acidity
max. 200
ppm HCI
MDI-01-03
Density 20 °C
approx. 1.23
g/cm³
DIN 51757
Phenylisocyanate content
max. 50
ppm
MDI-01-09
Coefficient of thermal expansion
6.59 . 10-4
K-1
Specific heat (cp)
approx. 1.51
kJ/kgK
Full data sheet
Contact
Close
Close
Construction materials
NWT M524-C64
Technical characteristics NWT M524-C64
Property
Test method
Unit
Specification nominal
Normal limitations
MAX.
MIN.
Area Weight
PTS-L-002
g/m2
30
33
27
Binder Content
PTS-L-003
%
7.5
9
6
Thickness
PTS-L-007
mm
0.29
0.33
0.25
Full data sheet
Contact
Close
TDS VR72
Characteristics TDS VR72
Tensile strength
Elongation
Standard condition
850/860
3.5/3.5
5% NaOH Solution
425/325
3.5/3.5
Fast Test
510/390
3.5/3.5
Full data sheet
Contact
Close
TEXIMPIANTI VR-73
Characteristics VR 73
Valor
Norma
Armatura
Tela
ISO 2113/1996
FINISH
GI 094
PESO gr./mq.
56 +/- 5%
ISO 3374/2000
SPESSORE mm.
0,09 +/- 5%
ISO 4603/1993
FILI AL cm.
7,4 +/- 2%
ISO 4602/1997
TRAME AL cm.
3,9 +/- 2%
ISO 4602/1997
FILATI UTILIZZATI :
FIBRA DI VETRO
ORDITO : EC 9 34 TEX
ISO 4602/1997
TRAMA : EC 9 68 TEX
ISO 4602/1997
RESISTENZA A TRAZIONE
ORDITO N/ 5cm. >600
ISO 4606/1995
TRAMA N/ 5cm. <500
ISO 4606/1995
RESINA SECCA APPORTATA :
gr./mq. 3,4 +/- 10%
ISO 1887/1995
Full data sheet
Contact
Close
Close
Close
History
Organization chart
Contact
Riberglas
Home
•
Riberglas
About
Riberglas
This author has not yet filled in any details.
So far Riberglas has created 0 blog entries.